Scuffing mechanisms of EN-GJS 400-15 spheroidal graphite cast iron against a 52100 bearing steel in a PAO lubricated reciprocating contact
نویسندگان
چکیده
منابع مشابه
A review on fatigue design of heavy section EN-GJS-400-18-LT ductile iron wind turbine castings
A comprehensive review of fatigue behavior and fatigue design of heavy section wind turbine castings made of ductile iron EN-GJS-400-18-LT is performed. Common metallurgical defects that are affecting fatigue behavior of this material were studied. Review of different researches on quantitative effect of chunky graphite and micro structure on fatigue behavior of EN-GJS-400-18-LT was perform...
متن کاملOn the Effect of Pouring Temperature on Spheroidal Graphite Cast Iron Solidification
This work is focused on the effect of pouring temperature on the thermal-microstructural response of an eutectic spheroidal graphite cast iron (SGCI). To this end, experiments as well as numerical simulations were carried out. Solidification tests in a wedge-like part were cast at two different pouring temperatures. Five specific locations exhibiting distinct cooling rates along the sample were...
متن کاملEffect of Surface Texturing on Cast Iron Reciprocating against Steel under Cyclic Loading in Boundary and Mixed Lubrication Conditions
This study investigates the effect of laser surface texturing on the friction behavior of grey cast iron reciprocating under boundary, mixed lubrication conditions and cyclic loading. Four geometrical parameters of micro-textures (feature depth, feature diameter, area fraction, and sliding direction) were studied using a design of experiments (DoE) approach. The results showed that depending on...
متن کاملA Thermal Elastohydrodynamic Lubricated Thrust Bearing Contact Model
A fully-coupled thermoelastic model for a fixed pad thrust bearing has been developed. Pressure, film thickness and three-dimensional temperature profiles were obtained by simultaneously solving the Reynolds, film thickness, energy and force balance equations using a combined finite difference and finite element method. The elastic deformation due to the pressure and the thermal distortion due ...
متن کاملa review on fatigue design of heavy section en-gjs-400-18-lt ductile iron wind turbine castings
a comprehensive review of fatigue behavior and fatigue design of heavy section wind turbine castings made of ductile iron en-gjs-400-18-lt is performed. common metallurgical defects that are affecting fatigue behavior of this material were studied. review of different researches on quantitative effect of chunky graphite and micro structure on fatigue behavior of en-gjs-400-18-lt was performed. ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Wear
سال: 2017
ISSN: 0043-1648
DOI: 10.1016/j.wear.2017.01.074