Screening on binary Ti alloy with excellent mechanical property and castability for dental prosthesis application
نویسندگان
چکیده
منابع مشابه
Screening on binary Ti alloy with excellent mechanical property and castability for dental prosthesis application
In the present study, the microstructure, mechanical property, castability, corrosion behavior and in vitro cytocompatibility of binary Ti-2X alloys with various alloying elements, including Ag, Bi, Ga, Ge, Hf, In, Mo, Nb, Sn and Zr, were systematically investigated, in order to assess their potential applications in dental field. The experimental results showed that all binary Ti‒2X alloys con...
متن کاملMechanical Characterisation and Biomechanical and Biological Behaviours of Ti-Zr Binary-Alloy Dental Implants
The objective of the study is to characterise the mechanical properties of Ti-15Zr binary alloy dental implants and to describe their biomechanical behaviour as well as their osseointegration capacity compared with the conventional Ti-6Al-4V (TAV) alloy implants. The mechanical properties of Ti-15Zr binary alloy were characterised using Roxolid© implants (Straumann, Basel, Switzerland) via ultr...
متن کاملSurface characteristics and castability of Zr-14Nb alloy dental castings.
The purpose of this study was to evaluate mechanical properties, surface characteristics and castability of Zr-14Nb dental castings. The mean 0.2% proof and ultimate tensile strengths of Zr-14Nb were approximately 68% and 76% those of Ti-6Al-7Nb, respectively, while they were comparable to Co-29Cr-6Mo. Elongation of Zr-14Nb was the highest of all alloys tested. The hardened reaction layer was f...
متن کاملBending Property of Super-Elastic Ti-Ni Alloy Dental Castings with Different Heat Treatments
Bending property of Ti-Ni alloy dental castings was evaluated in comparison with that of Co-Cr alloy in a cantilever test. Heat treatment effect on the bending property was also investigated in relation to phase transformation. Ti-50.85Ni (mol%) alloy was used, and the shape of bending test specimens was half-rounded in cross section, 2.0mm in diameter. The bending test was carried out at 310K....
متن کاملDental casting of superelastic Ni-Ti alloy.
Rods of Ni-43.5wt% Ti alloy were prepared under various casting conditions. Specimens which were melted in a cordierite crucible and cast in a phosphate-bonded investment mold had less strength and elongation than those melted in a copper crucible and cast in a phosphate-bonded investment mold. All castings exhibited superelasticity at room temperature. The upper limit of recoverable strain was...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scientific Reports
سال: 2016
ISSN: 2045-2322
DOI: 10.1038/srep37428