Rupture strength and fracture toughness of WC-Co alloys.
نویسندگان
چکیده
منابع مشابه
New results on the relationship between hardness and fracture toughness of WC-Co hardmetal
Two sets of WC-Co grades were produced, with cobalt content ranging from 3 to 50 wt.%. The mean grain size of the two sets was 2.2 and 6 ~tm respectively. The two sets of grades were used to investigate the relationship between hardness and fracture toughness. It was found that at constant WC grain size the relationship is linear. It was also found that in the low toughness range, grades of equ...
متن کاملEffect of WC/Co coherency phase boundaries on Fracture toughness of the nanocrystalline cemented carbides
The effect of coherency WC/Co phase boundaries on the fracture toughness of the nanocrystalline WC-Co cemented carbides is studied by MD simulation method. The simulation results show that the nanocrystalline WC-Co cemented carbides with coherency WC/Co phase boundaries has higher fracture toughness than that without coherency WC/Co phase boundaries. Moreover, the mechanism of why coherency WC/...
متن کاملEvaluation of fracture strength of TiN thin films deposited on WC-Co substrate
To evaluate the fracture strength of TiN thin films deposited on the hard metal substrate WC-Co, and to investigate the influence of the deposition conditions (bias voltage VB) on the fracture strength of TiN thin films, the sphere indentation test was carried out to determine the ring crack initiation strength σf,m in TiN thin films deposited on two kinds of WC-Co substrates differing in hardn...
متن کاملTEM INVESTIGATIONS OF WC-Co ALLOYS AFTER CREEP EXPERIMENTS
Carbide tungsten cobalt alloys were deformed in compression or in three point bending in a temperature range 1000-1350°C and in a stress domain 30-1000MPa. In these conditions, the stress exponent n of WC-CO alloys is a function of only the cobalt volurnic ratio and tends tow rds n = 1 for pure B carbide. The apparent activation energy is 550 kj mole. T.E.M. investigations on pure carbide defor...
متن کاملFRACTURE AND FATIGUE BEHAVIOR OF WC-Co AND WC-CoNi CEMENTED CARBIDES
The fracture and fatigue characteristics of several cemented carbide grades are investigated as a function of their microstructure. In doing so, the influence of binder chemical nature and content (Co and 76wt%Co-24wt%Ni), as well as carbide grain size on hardness, flexural strength, fracture toughness and fatigue crack growth (FCG) behavior is evaluated. Mechanical testing is combined with a d...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1987
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.34.181