Room-Temperature Superplasticity in an Ultrafine-Grained Magnesium Alloy
نویسندگان
چکیده
منابع مشابه
Mechanical Behavior of an Ultrafine/Nano Grained Magnesium Alloy
The application of magnesium alloys is greatly limited because of their relatively low strength and ductility. An effective way to improve the mechanical properties of magnesium alloy is to refine the grains. As the race for better materials performance is never ending, attempts to develop viable techniques for microstructure refinement continue. Further refining of grain size requires, however...
متن کاملEvolution of texture in an ultrafine and nano grained magnesium alloy
The evolution of texture was discussed during the formation of ultra-fine and nano grains in a magnesium alloy severely deformed through accumulative back extrusion (ABE). The microstructure and texture obtained after applying multiple deformation passes at temperatures of 100 and 250°C were characterized. The results showed that after single ABE pass at 100°C an ultrafine/nano grained microstr...
متن کاملevolution of texture in an ultrafine and nano grained magnesium alloy
the evolution of texture was discussed during the formation of ultra-fine and nano grains in a magnesium alloy severely deformed through accumulative back extrusion (abe). the microstructure and texture obtained after applying multiple deformation passes at temperatures of 100 and 250°c were characterized. the results showed that after single abe pass at 100°c an ultrafine/nano grained microstr...
متن کاملRecrystallization texture during ECAP processing of ultrafine/nano grained magnesium alloy
An ultrafine/nano grained AZ31 magnesium alloy was produced through four-pass ECAP processing. TEM microscopy indicated that recrystallized regions included nano grains of 75 nm. Pole figures showed that a fiber basal texture with two-pole peaks was developed after four passes, where a basal pole peak lies parallel to the extrusion direction (ED) and the other ~20° away from the transverse dire...
متن کاملDynamic Micro-strain Analysis of Ultrafine-grained Aluminum Magnesium alloy using Digital Image Correlation
Tensile tests were performed in situ on an ultrafine-grained (UFG) Al-Mg alloy using a micro-tensile module in a scanning electron microscope (SEM). The micro-strain evolution was tracked and measured using digital image correlation (DIC). A fine random speckle pattern was required to achieve high resolution and accuracy of strain measurement using DIC. To produce the speckle pattern, a pattern...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Scientific Reports
سال: 2017
ISSN: 2045-2322
DOI: 10.1038/s41598-017-02846-2