Room-temperature larger-scale highly ordered nanorod imprints of ZnO film
نویسندگان
چکیده
منابع مشابه
Room-temperature larger-scale highly ordered nanorod imprints of ZnO film.
Room-temperature large-scale highly ordered nanorod-patterned ZnO films directly integrated on III-nitride light-emitting diodes (LEDs) are proposed and demonstrated via low-cost modified nanoimprinting, avoiding a high-temperature process. with a 600 nm pitch on top of a critical 200 nm thick Imprinting ZnO nanorods of 200 nm in diameter and 200 nm in height continuous ZnO wetting layer, the l...
متن کاملRoom-temperature nonequilibrium growth of controllable ZnO nanorod arrays
In this study, controllable ZnO nanorod arrays were successfully synthesized on Si substrate at room temperature (approx. 25°C). The formation of controllable ZnO nanorod arrays has been investigated using growth media with different concentrations and molar ratios of Zn(NO3)2 to NaOH. Under such a nonequilibrium growth condition, the density and dimension of ZnO nanorod arrays were successfull...
متن کاملFabrication of Highly Ordered Gold Nanorods Film Using Alumina Nanopores
A simple method for fabrication of highly ordered gold nanorod film is introduced in this article. The procedure is based on thermal evaporation of gold into a porous anodic alumina film (PAA). The PPA film was fabricated by combining the hard and mild anodization. This combination effectively decreases the processing time of fabrication of highly ordered porous anodic alumina film with c...
متن کاملStudy on room temperature gas-sensing performance of CuO film-decorated ordered porous ZnO composite by In2O3 sensitization
For the first time, ordered mesoporous ZnO nanoparticles have been synthesized by a template method. The electroplating after chemical plating method was creatively used to form copper film on the surface of the prepared ZnO, and then a CuO film-decorated ordered porous ZnO composite (CuO/ZnO) was obtained by a high-temperature oxidation method. In2O3 was loaded into the prepared CuO film-ZnO b...
متن کاملRoom temperature synthesis and optical properties of small diameter (5 nm) ZnO nanorod arrays.
We report a simple wet-chemical synthesis of ∼5 nm diameter ZnO nanorod arrays at room temperature (20 °C) and normal atmospheric pressure (1 atm) and their optical properties. They were single crystalline in nature, and grew in the [001] direction. These small diameter ZnO nanorod arrays can also be synthesized at 0 °C. Control experiments were also conducted. On the basis of the results, we p...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Optics Express
سال: 2013
ISSN: 1094-4087
DOI: 10.1364/oe.21.026846