Room-temperature BTEX sensing characterization of nanostructured ZnO thin films
نویسندگان
چکیده
منابع مشابه
Characterization of nanostructured ZnO thin films deposited through vacuum evaporation
This work presents a novel technique to deposit ZnO thin films through a metal vacuum evaporation technique using colloidal nanoparticles (average size of 30 nm), which were synthesized by our research group, as source. These thin films had a thickness between 45 and 123 nm as measured by profilometry. XRD patterns of the deposited thin films were obtained. According to the HRSEM micrographs wo...
متن کاملZnO Nanoparticles/Reduced Graphene Oxide Bilayer Thin Films for Improved NH3-Sensing Performances at Room Temperature
ZnO nanoparticles and graphene oxide (GO) thin film were deposited on gold interdigital electrodes (IDEs) in sequence via simple spraying process, which was further restored to ZnO/reduced graphene oxide (rGO) bilayer thin film by the thermal reduction treatment and employed for ammonia (NH3) detection at room temperature. rGO was identified by UV-vis absorption spectra and X-ray photoelectron ...
متن کاملCharacterization of ZnO Thin Films
ZnO is a strategic material for various photonic applications. We present our results on characterization of thin films of ZnO grown by sol-gel spin and RF sputtering methods. The characterization techniques involved ellipsometry, scanning electron microscopy with energy dispersive analysis, X-ray diffraction and scanning tunneling microscopy. Microstructural characterization of the films using...
متن کاملStudies on sol-gel dip-coated nanostructured ZnO thin films
Nanostructured ZnO thin films were prepared by sol-gel dip coating technique. Zinc acetate and ammonium hydroxide were used as precursors and ethanol was as solvent. Ammonium hydroxide (NH4OH) solution was added drop-wise under vigorous stirring to obtain the sol-gel of different pH (varying from 6.9 to 7.2). ZnO thin films were obtained by dipping the glass substrates for few seconds and then ...
متن کاملRoom-Temperature Humidity Sensing Using Graphene Oxide Thin Films
In this article, we report on a room-temperature humidity sensing device using graphene oxide (GO) thin films synthesized by chemical exfoliation. Changes in the device conductivity are measured for varying relative humidity in the experimental chamber. Experiments are carried out for relative humidity varying from 30% to 95%. We observe a difference in the results obtained for low relative hum...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Asian Ceramic Societies
سال: 2019
ISSN: 2187-0764
DOI: 10.1080/21870764.2019.1579401