Retrieval Analysis And Principal Variable Analysis Of 127 M2a-38 Mm™ Metal On Metal Hip Replacements

CoCrMo metal-on-metal hip replacements.

After the rapid growth in the use of CoCrMo metal-on-metal hip replacements since the second generation was introduced circa 1990, metal-on-metal hip replacements have experienced a sharp decline in the last two years due to biocompatibility issues related to wear and corrosion products. Despite some excellent clinical results, the release of wear and corrosion debris and the adverse response o...

Metal-on-Metal Hip Retrieval Analysis: A Case Report

This is a case report involving a single case with severe bone and soft tissue destruction in a young male patient with a 10-year-metal on-metal total hip arthroplasty. Following complete aseptic erosion of the affected hip greater trochanter and abductor muscles, the hip was revised for recurrent instability. Histological examination of the patient's periprosthetic tissues, serological studies...

Effect of microseparation on contact mechanics in metal-on-metal hip replacements-A finite element analysis.

Some early failures of metal-on-metal (MoM) hip replacements associated with elevated wear have caused concerns for the use of this bearing combination. Simulator studies have shown that microseparation and its associated rim contact and edge loading may produce the most severe wear in MoM bearings. It is generally recognized that this high wear can be attributed to the high contact stress of t...

Follow-up of patients with metal-on-metal hip replacements.

Heart failure after conventional metal-on-metal hip replacements

Background and purpose - It is unclear whether metal particles and ions produced by mechanical wear and corrosion of hip prostheses with metal-on-metal (MoM) bearings have systemic adverse effects on health. We compared the risk of heart failure in patients with conventional MoM total hip arthroplasty (THA) and in those with metal-on-polyethylene (MoP) THA. Patients and methods - We conducted a...