Resistance of nanofill and nanohybrid resin composites to toothbrush abrasion with calcium carbonate slurry
نویسندگان
چکیده
منابع مشابه
Resistance of nanofill and nanohybrid resin composites to toothbrush abrasion with calcium carbonate slurry.
The aim of this study was to investigate the wear of four nanofilled resin composites using simulated toothbrushing for 50,000 cycles with calcium carbonate slurry. The depth of abrasion and roughness (Ra) were measured after each 10,000 brushing cycle. The surface texture of the worn samples was examined by SEM.The wear depths of the nanofill Filtek Supreme XT (FIL), the nanohybrides Grandio (...
متن کاملIn vitro toothbrushing abrasion of dental resin composites: packable, microhybrid, nanohybrid and microfilled materials.
This study evaluated weight loss and surface roughening after toothbrushing of different resin composites: one packable (Solitaire 2, Heraeus Kulzer), one microhybrid (Charisma, Heraeus Kulzer), one nanohybrid (Simile, Pentron) and one microfilled (Durafill VS, Heraeus Kulzer). Cylindrical specimens (n = 20) were prepared. Half of the samples were submitted to 60,000 strokes, at 4 Hz, with a de...
متن کاملSurface roughness and wear of resin cements after toothbrush abrasion.
Increased surface roughness and wear of resin cements may cause failure of indirect restorations. The aim of this study was to evaluate quantitatively the surface roughness change and the vertical wear of four resin cements subjected to mechanical toothbrushing abrasion. Ten rectangular specimens (15 × 5 × 4 mm) were fabricated according to manufacturer instructions for each group (n = 10): Nex...
متن کاملSynthesis and Characterization of Polyamide-66/Calcium Carbonate Composites
Polyamide-66(PA66)/CaCO3 micro- and nano-composites were prepared using a polymer solution method at filler loading of 0, 1, 2 and 3 weight percent. Nano-size of CaCO3 was synthesized by micro-emulsion technique. The material was characterized by XRD, SEM, FTIR and UV-VIS techniques. XRD results of composites suggested that CaCO3 particles are found in the amorphous phase of the semi-crystallin...
متن کاملAbrasion Resistance of Cement-Based Composites
Cement-based composites are among the most widely-used construction materials due to their low cost, high compressive strength, high durability, versatility, and easy-handling. Unfortunately, cement-based composites are intrinsically porous and may deteriorate as a result of exposure to harsh environments or poor construction quality. Over the last few decades, most research has focused on the ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Dental Materials Journal
سال: 2009
ISSN: 1881-1361,0287-4547
DOI: 10.4012/dmj.28.708