Fatigue behavior of case hardened parts depend to a great extent on the type of residual stresses developed in the components. Topography and metallurgical effects were the two elements which contribute much to surface integrity. Micro hardness of the gas carburized (EN 33 and EN 36) and Induction hardened (AISI 1040 and AISI 6150) specimens obtained during experiments, showed that there was gr...
متن کاملNondestructive evaluation of residual stresses in case hardened steels by magnetic anisotropy measurements
This paper reports on a recent study aimed at developing the stress-induced magnetic anisotropy (SMA) technique for characterizing residual stresses in case hardened steel components. The results of SMA measurements performed on flat induction hardened steel discs with different case depths confirm the feasibility of detecting principal stress axes by measuring the angular variation of magnetic...
متن کاملStresses in nanocrystalline materials
Thin film Ni-Cu diffusion couples (individual layer thicknesses: 50 nm) were prepared by direct-current magnetron sputtering on silicon substrates. Interdiffusion and solid-solution formation, the associated changes of microstructure and the evolution of mechanical stresses of the Ni-Cu diffusion couples during thermal treatments were investigated employing ex-situ X-ray diffraction phase and t...
متن کاملResidual Stresses Measurement in Hollow Samples Using Contour Method
Residual stresses are created usually undesirably during manufacturing processes, including casting, welding, metal forming, etc. Residual stresses alone or in combination with other factors can cause the destruction and fracture of components or significant decline in their service life. Therefore, it is crucial to measure the residual stresses. Contour method is a destructive testing method c...
متن کاملA model for aging under deformation field, residual stresses and strains in soft glassy materials.
A model is proposed that considers aging and rejuvenation in a soft glassy material as, respectively, a decrease and an increase in free energy. The aging term is weighted by an inverse of characteristic relaxation time suggesting that greater mobility of the constituents induces faster aging in a material. A dependence of relaxation time on free energy is proposed, which under quiescent condit...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Open Materials Science Journal
سال: 2010
ISSN: 1874-088X
DOI: 10.2174/1874088x010040300092