Residual Stresses and Fatigue of Mild Steel
نویسندگان
چکیده
منابع مشابه
Hydrogen Assisted Cracking in Pearlitic Steel Rods: The Role of Residual Stresses Generated by Fatigue Precracking
Stress corrosion cracking (SCC) of metals is an issue of major concern in engineering since this phenomenon causes many catastrophic failures of structural components in aggressive environments. SCC is even more harmful under cathodic conditions promoting the phenomenon known as hydrogen assisted cracking (HAC), hydrogen assisted fracture (HAF) or hydrogen embrittlement (HE). A common way to as...
متن کاملResidual Stresses and Fatigue of Surface Treated Welied Specimens
An e x p e r i m e n t a l program was under t aken t o e v a l u a t e t h e e f f e c t of induced compress ive s t r e s s e s due t o v a r i o u s peen ing and t h e r m a l t r e a t m e n t s on t h e f a t i g u e l i f e of a b u t t welded medium s t r e n g t h s t e e l (Cb-50). R e s i d u a l s t r e s s e s were measured u s i n g x-ray d i f f r a c t i o n and t h e r e s u l t...
متن کاملSurface Residual Stresses in Dry Turning of 0.45% C Steel
Residual stresses in a surface layer determine many exploitation characteristics of machined surface. Depending on their kind and the type of applied loading, the influence of residual stresses can be negative or positive. Tensile residual stresses usually exert highly detrimental impact on several functional aspects such as strength, fatigue life, corrosion, wear resistance, etc., whereas comp...
متن کاملResidual Stress Analysis and Fatigue Assessment of Welded Steel Structures
.............................................................................................................................. .i APPENDED PAPERS ............................................................................................................... ii PAPERS NOT INCLUDED IN THIS THESIS........................................................................ iii DIVISION OF WORK BETWEEN ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1969
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.33.8_916