Research on Stainless Steels for Pulp, Dye and Bleaching Industry
نویسندگان
چکیده
منابع مشابه
Y Studies on Austenitic Stainless Steels
Abstract--In this investigation, the fracture surfaces of SS 304 and SS 316 austenitic steels were analysed using the X-ray fractography technique. In both cases, a decrease in the austenite content was observed at the fracture surface as a result of deformation induced martensite, indicating a linear relation with Km~ within the stable crack growth region. The presence of this martensite was f...
متن کاملEnzymatic Bleaching of Wood Pulp
The dark colour of kraft pulp after the wood chips have been heated at high temperature with NaOH solution is caused by lignin (a complex phenolic polymer) still attached to the cellulose fibres. Traditionally this pulp is treated with chlorine to bleach the pulp to make it suitable for paper making. Unfortunately this leads to the formation of some potentially toxic chlorophenolic compounds of...
متن کاملLow-Temperature Carburization of Austenitic Stainless Steels
LOW-TEMPERATURE CARBURIZATION is a gaseous carburization process performed at atmospheric pressure, at temperatures where the kinetics of substitutional diffusion are very slow. Low-temperature carburization hardens the surface of austenitic stainless steels through the diffusion of interstitial carbon, without the formation of carbides. The surface must be activated, by modification and remova...
متن کاملPulp reaction to vital bleaching.
This study evaluated the histological changes in dental pulp after nightguard vital bleaching with 10% carbamide peroxide gel. Fifteen patients between 12 and 26 years of age with caries-free first premolars scheduled for orthodontic extraction were treated with 10% Opalescence (Ultradent Products, Inc). Tooth #5 had four days of bleaching, tooth #12 was treated for two weeks, tooth #21 was ble...
متن کاملStudy on Oxidation of Stainless Steels During Hot Rolling
The oxidation of stainless steels 304 and 304L during hot rolling is studied in this paper. Results show the oxide scale thickness decreases significantly with an increase of reduction, and the oxide scales of both 304 and 304L stainless steels were found more deformable than the steel substrate. Surface roughness shows a complicated transfer during the hot rolling process due to the complexity...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: The Journal of the Japan Institute of Metals.B
سال: 1950
ISSN: 2433-7471
DOI: 10.2320/jinstmet1950b.14.8_32