Research on Precipitate Behavior during Holding Process of X80 Pipeline Steel
نویسندگان
چکیده
منابع مشابه
Effect of Nanosized NbC Precipitates on Hydrogen Diffusion in X80 Pipeline Steel
In this paper, the effects of dispersed 3~10 nm NbC precipitates on hydrogen diffusion in X80 pipeline steel were investigated by means of high resolution transmission electron microscopy (HRTEM), electrochemical hydrogen permeation, and thermal desorption spectroscopy (TDS). The relationship between hydrogen diffusion and temperature was determined for Nb-free X80 and 0.055 wt% Nb X80 steel. T...
متن کاملEFFECTS OF ANODIC PROTECTION ON SCC BEHAVIOR OF X80 PIPELINE STEEL IN HIGH-pH CARBONATE-BICARBONATE SOLUTION WPŁYW OCHRONY ANODOWEJ NA NAPRĘŻENIOWE PĘKANIE KOROZYJNE STALI TYPU X80 Z ZASTOSOWANIEM NA RUROCIĄGI W ROZTWORZE BUFOROWYM O WYSOKIM pH
The potentiodynamic polarization test and slow strain rate tensile tests of X80 pipeline steel were performed in 0.5M Na2CO3-1M NaHCO3 solution to study the electrochemical and stress corrosion cracking properties. The results of potentiodynamic polarization test show that there is an obvious stable passive region, about from 0v to 0.8V (SCE), indicating that anodic protection is feasible. The ...
متن کاملCorrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment
The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with t...
متن کاملEffect of Heat Input of Submerged Arc Welding Process on the Corrosion Behavior of API X42 Gas Pipeline Steel Weld Joint
The effect of heat input of submerged arc welding process on the corrosion bahavior of weld metal of API X42 gas pipeline steel weld joint was investigated. For this purpose, 6 annealed sheets of 15mm thickness were prepared from the X42 microalloyed steel. Submerged arc welding process with varying heat input of 37.8, 18.9 and 12.6 kJ/mm was used for joint welding. Then potentiodynamic polariz...
متن کاملEffect of Heat Input of Submerged Arc Welding Process on the Corrosion Behavior of API X42 Gas Pipeline Steel Weld Joint
The effect of heat input of submerged arc welding process on the corrosion bahavior of weld metal of API X42 gas pipeline steel weld joint was investigated. For this purpose, 6 annealed sheets of 15mm thickness were prepared from the X42 microalloyed steel. Submerged arc welding process with varying heat input of 37.8, 18.9 and 12.6 kJ/mm was used for joint welding. Then potentiodynamic polariz...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: MATEC Web of Conferences
سال: 2016
ISSN: 2261-236X
DOI: 10.1051/matecconf/20166705006