Research on Mechanical Properties of Bamboo Modified with Melamine-Formaldehyde Resin
نویسندگان
چکیده
منابع مشابه
Rattan Cane Modified with Polyethylene Glycol Melamine-Urea-Formaldehyde Resin
To effectively improve the strength of Plectocomia pierreana rattan cane without reducing its toughness, the cane was impregnated with a new water-soluble melamine-urea-formaldehyde (MUF) resin modified with low-molecular-weight polyethylene glycol (PEG), marked as PMUF. The PMUF synthetic process was optimized using an orthogonal test L9(3). Results showed that the dimensional stability, densi...
متن کاملMelamine-modified urea formaldehyde resin for bonding particleboards
For the development of a cost-effective melamine-modified urea formaldehyde resin (MUF), the study evaluated the effects of reaction pH and melamine content on resin properties and bond performance of the MUF resin adhesive systems. Eight resins, each with three replicates, were prepared in a factorial experiment that included two formulation variables: two reaction pHs (i.e., 4.5 and 8.0) and ...
متن کاملMicroscopic Characterization of Modified Phenol- Formaldehyde Resin Penetration of Bamboo Surfaces and its Effect on Some Properties of Two-Ply Bamboo Bonding Interface
The bonding interface between bamboo elements and adhesives is presumed to be significantly influenced by the degree of adhesive penetration into the porous network of interconnected cells of bamboo surfaces. In the study presented here, the average depth and effective depth of phenol-formaldehyde resin (PF) modified by different contents of lower-molecular weight (LMW) PF on bamboo surface wer...
متن کاملMelamine-Bridged Alkyl Resorcinol Modified Urea– Formaldehyde Resin for Bonding Hardwood Plywood
A powdery product was obtained by the reaction of methylolated melamine with alkyl resorcinols to form melamine-bridged alkyl resorcinols (MARs). The effects of the addition of this powder on the bonding strength and formaldehyde emission of urea–formaldehyde (UF) resins were investigated. Three types of UF resins with a formaldehyde/urea molar ratio of 1.3 synthesized by condensation at pH 1.0...
متن کاملEffect of Modification with Phenol Formaldehyde Resin on the Mechanical Properties of Wood from Chinese Fir
Samples of Chinese fir were treated with either low-molecular-weight or commercial phenol-formaldehyde (PF) resins. The macroand micromechanical properties of the treated and untreated samples were determined. The average longitudinal tensile modulus of elasticity (MOE) was 30.88% larger for the samples treated with the low-molecular-weight PF resin than it was for the untreated samples. The av...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: DEStech Transactions on Engineering and Technology Research
سال: 2017
ISSN: 2475-885X
DOI: 10.12783/dtetr/apetc2017/11086