Relation of threshold levels fatigue crack development in low-alloy steel under harmonic and operational loading
نویسندگان
چکیده
منابع مشابه
Accelerated Threshold Fatigue Crack Growth Effect – Powder Metallurgy Aluminum Alloy
Fatigue crack growth (FCG) research conducted in the near threshold regime has identified a room temperature creep crack growth damage mechanism for a fine grain powder metallurgy (PM) aluminum alloy (8009). At very low ∆K, an abrupt acceleration in room temperature FCG rate occurs at high stress ratio (R = Kmin/Kmax). The near threshold accelerated FCG rates are exacerbated by increased levels...
متن کاملStrip yield modelling of fatigue crack under variable amplitude loading
The results from ‘strip yield’ approach of the FASTRAN type models of plasticity induced crack closure effects of fatigue cracks subjected to variable amplitude loadings are presented. The strip yield results are compared with authors’ finite element (FE) and experimental results. It has been observed that the strip yield model is seen to be fundamentally limited by choice of α (constraint fact...
متن کاملEffect of Boundary Condition on Pre-Existing Crack Under Fatigue Loading
In this paper, the present investigation has been conducted keeping in mind some of the problems concerning the crack propagation direction and growth under constant loading in an inclined crack geometry. The present studies mainly focused on the development and modifications in the crack growth criterion to account the biaxial, shear loading and number of stress terms. Existing criteria for th...
متن کاملAnalyses of Fatigue and Fatigue-crack Growth under Constant- and Variable-amplitude Loading
Studies on the growth of small cracks have led to the observation that fatigue life of many engineering materials is primarily “crack growth” from micro-structural features, such as inclusion particles, voids, slip-bands or from manufacturing defects. This paper reviews the capabilities of a plasticity-induced crack-closure model to predict fatigue lives of metallic materials using “small-crack...
متن کاملUltra low cycle fatigue of welded steel joints under multiaxial loading
Ultra low cycle fatigue (ULCF) is a phenomenon that can be summarily defined as the deterioration of material properties under high amplitude cyclic loading, under which failure is reached typically within ten to twenty cycles. This phenomenon is observed in extreme loading scenarios such as earthquakes or exceptional winds where large cyclic strains are expected. Particularly sensitive are str...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOP Conference Series: Materials Science and Engineering
سال: 2021
ISSN: 1757-899X
DOI: 10.1088/1757-899x/1023/1/012015