Relation between Hot Ductility and Grain Boundary Embrittlement of Low-Carbon Killed Steels
نویسندگان
چکیده
منابع مشابه
Determining the Hot Deformation Temperature Range of Medium Carbon Ni-Cr-Mo Low Alloy Steels using Hot Tensile and Hot Torsion Tests
The aim of this study was to investigate the suitable temperature range for hot deformation of three medium carbon Ni-Cr-Mo low alloy steels by hot tensile and hot torsion tests. Hot tensile tests were carried out in the te,prature range of 850-1150°C at a constant strain rate of 0.1 s-1 until fracture. Then, the tensile flow behavior, hot ductility and microstructural evolution of the steels w...
متن کاملPrevention of Hydrogen Embrittlement in Steels
The essential facts about the nature of the hydrogen embrittlement of steels have now been known for 140 years. It is diffusible hydrogen that is harmful to the toughness of iron. It follows, therefore, that the harmful influence of diffusible hydrogen can be mitigated by preventing its entry into steel or by rendering it immobile once it penetrates the material. This review deals with the meth...
متن کاملPrediction of Deformation Resistance of Low Carbon Steels during Hot Rolling
Phenomenological approach to the description of deformation resistance behaviour of steel and its microstructure development under the service hot rolling condition is still the most common useful and powerful. Utilising different experimental equipment such as torsion plastometer [1-5], compression plastometer [6-9], or advanced laboratory mills [10, 11] as well as different deformation techni...
متن کاملGrain Boundary Segregation in Commercial Nuclear Reactor Pressure Vessel Steels
Grain boundary (GB) segregation of impurity/solute atoms in surveillance test specimens of a commercial western-type pressurized water reactor pressure vessel (RPV) steel has been observed by using state-of-the-art 3D atom probe (3DAP) field ion microscope (laser-assisted local electrode-type atom probe: laser-LEAP). The GB segregation is considered to be an origin of the embrittlement of the R...
متن کاملCharacteristics of Hydrogen Embrittlement, Stress Corrosion Cracking and Tempered Martensite Embrittlement in High-strength Steels
Characteristics of tempered martensite embrittlement (TME), hydrogen embrittlement (HE), and stress corrosion cracking (SCC) in high-strength steels are reviewed. Often, it is important to determine unambiguously by which of these mechanisms failure occurred, in order to suggest the right actions to prevent failure recurrence. To this aim, samples made of high-strength AISI 4340 alloy steel wer...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Tetsu-to-Hagane
سال: 1979
ISSN: 0021-1575,1883-2954
DOI: 10.2355/tetsutohagane1955.65.9_1410