Relation between fatigue strength and reinforcement shape of simulated butt-welded joint.
نویسندگان
چکیده
منابع مشابه
Relation between Residual Stress and Fatigue Strength for Electron Beam Welded Joints of Sheet Metal
Residual stresses in welds significantly affect the fatigue strength and stress corrosion crack resistance of the weld joint, and therefore, numerous studies have been made about the effects. The residual stress induced by electron beam welding (EBW) has also been researched in various approaches, but many of the study reports dealt with thick plates (50 mm or thicker) only.1–5) This was becaus...
متن کاملThe Fatigue Strength of Fillet Welded Connections
This report describes a study of the fatigue behavior of fillet welded joints stressed perpendicular to the weld line. The study included an experimental phase in which the stiess-life and cracking behavior of load and nonload carrying fillet weld joints was determined. This experimental study concentrated on the fatigue behavior in the transition region between high and low cycle fatigue 3 5 (...
متن کاملStress Intensity Factor Expression for Welded Butt Joint with Undercut and Inclined Lack of Penetration Defects considering the Effect of Joint Shape
In this paper, the stress intensity factor (SIF) expression for defected butt welds containing undercut and inclined lack of penetration (LOP) subject to far-field tensile stress is derived. Some of the standards such as ISO 5817 and BS EN 25817 have specified allowable limits for the length of the undercut and LOP defects and for the height of the weld. In addition, EN 29692 standard has deter...
متن کاملFinite Element Analysis of Effect of Weld Toe Radius and Plate Thickness on Fatigue Life of Butt Welded Joint
Mechanical parts during service may be subjected to cyclical loading and high stresses, which make fatigue life prediction extremely important. The finite element method is commonly used in research institutions and industry in order to estimate life span of mechanical parts. In this study, an experimental investigation of the geometrical dimensions and mechanical properties of a weld joint, an...
متن کاملImproving Fatigue Strength of Welded Joints by Ultrasonic Impact Treatment
Enhancement in fatigue performance of welded joints by Ultrasonic Impact Treatment (UIT) was evaluated with large-scale rolled beam and built-up specimens having yield strength of 345 to 760 MPa. Eighteen rolled-beam specimens having welded details at cover plates and transverse stiffeners and eight built-up specimens having only transverse stiffener details were fatigue tested after treating t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
سال: 1991
ISSN: 0288-4771
DOI: 10.2207/qjjws.9.31