Relation between Corrosion Rate of Magnesia Refractories by Molten Slag and Penetration Rate of Slag into Refractories
نویسندگان
چکیده
منابع مشابه
Interaction Mechanism between Refractory and Melts in Iron Bath Smelting Reduction Process
The corrosion behavior of three sorts of refractories based on alumina-graphite were studied by immersion tests. The melts included smelting reduction molten slag and corresponding carbon saturated molten iron. The influence of test temperature, FeO content in slag and specimen rotative velocity on the corrosion rate of refractories was examined. By means of SEM and EDS, the microstructure chan...
متن کاملTHEORY, EXPERIMENT AND PRACTICE OF SLAG ATTACK OF REFRACTORIES
Penetration and dissolution mechanisms are reviewed for predominantly single-phase oxide, two phase oxide and oxide-carbon composite refractories by liquid silicate slags. Theoretical models of these processes, as well as static (sessile drop, dipping and crucible) and dynamic (rotating finger and rotary slag) experimental tests, along with their practical limitations are considered. Direct (co...
متن کاملInvestigations of Calcium Aluminate Slag Penetration to MgO Monolithic Refractories in Steelmaking Process
In this study, slag penetration into a magnesia refractory monolithic was investigated by the crucible test method. A synthetic calcium aluminate slag system has been used to study commercial magnesia mix refractory for 1, 2, 3, 4, 5 and 6 hours at 1450°C and 1600°C. It has been shown that the penetration rate is controlled by a diffusion mechanism at 1450°C. In this case, capillaries are the ...
متن کاملinvestigations of calcium aluminate slag penetration to mgo monolithic refractories in steelmaking process
in this study, slag penetration into a magnesia refractory monolithic was investigated by the crucible test method. a synthetic calcium aluminate slag system has been used to study commercial magnesia mix refractory for 1, 2, 3, 4, 5 and 6 hours at 1450°c and 1600°c. it has been shown that the penetration rate is controlled by a diffusion mechanism at 1450°c. in this case, capillaries are the ...
متن کاملNEW REFRACTORY MATERIALS FOR THE COPPER INDUSTRY
Wear of various basic refractory materials to substitute to currently used magnesia chrome bricks has been studied, measuring matte and slag penetration and dissolution, through different cup and rotary slag tests. High magnesia with and without impregnation, magnesia graphite, magnesia-alumina spinel with and without impregnation, olivine-magnesia and olivine magnesia- graphite bricks, as well...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 1993
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.101.533