Microstructural Characterisation of Chromium Slags
J. Burja, F. Tehovnik, F. Vode, B. Arh, Institute of Metals and Technology, Ljubljana, Slovenia In this chromium slags that form during melting of chromium alloyed steels are examined. During melting and oxidation of these steel grades a considerable amount of chromium is lost, and gained back with slag reduction. Laboratory experiments were performed to study the mechanism of chromium oxide re...
متن کاملPhotocatalytic Removal of Hexavalet Chromium from Aqueous Solution Using Zinc Oxide Nanoparticle Stabilized On Zeolite
Backgrounds & objectives: Heavy metals, such as chromium, are the most common pollutants usually found in high concentrations in industrial wastewater and cause damages to aquatic environments and endanger the health of living organisms, especially human. Therefore, the purpose of this research was to investigate the photocatalytic removal of hexavalent chromium from aqueous solution using UV/Z...
متن کاملFeasibility of recovering metals from associated slags
The associated mineral ore accompanying Valuable Metal Compounds (VMC) have been usually treated in a smelting furnace ,such as Blast Furnace, Reverberatory, Blowing Furnace, hence the VMC were mostly concentrated into the molten associated slags and separated from liquid metals. So the associated slags become an important man-made resources (Table I), in which the VMC exist dispersively in var...
متن کاملMicrobial Reduction of Hexavalent Chromium
Publication 1. A. Manceau et al, “Quantitative Zn speciation in smelter-contaminated soils by EXAFS spectroscopy,” Am. J. Sci. (in press, 2000). Figure 3 (top) Soil samples were taken at several depths from a contaminated site. (bottom) Model compounds derived from polarized-EXAFS data at the ESRF and μ-EXAFS data at the ALS provide a good fit with powder-EXAFS spectra from a soil sample, there...
متن کاملPulsed plasma deposition of chromium oxide/chromium-cermet coatings
A novel radio frequency magnetron sputtering method for the deposition of composite films which consist of chromium oxide and chromium ~Cr2O3/Cr-cermet! is presented. As an extension to conventional reactive sputtering of a Cr target in an argon and oxygen atmosphere the oxygen flow into the process chamber is switched periodically on and off. This leads to an oscillating oxygen partial pressur...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Revista de Metalurgia
سال: 2005
ISSN: 1988-4222,0034-8570
DOI: 10.3989/revmetalm.2005.v41.iextra.1073