Recrystallization Texture of Cold-Rolled 50-Iron 50-Nickel Alloy
نویسندگان
چکیده
منابع مشابه
Statistical analysis on static recrystallization texture evolution in cold-rolled AZ31 magnesium alloy sheet.
Cast AZ31B-H24 magnesium alloy, comprising Mg with 3.27 wt% Al and 0.96 wt% Zn, was cold rolled and subsequently annealed. Global texture evolutions in the specimens were observed by X-ray diffractometry after the thermomechanical processing. Image-based microstructure and texture for the deformed, recrystallized, and grown grains were observed by electron backscattered diffractometry. Recrysta...
متن کاملGrain Boundary Evolution of Cold-Rolled FePd Alloy during Recrystallization at Disordering Temperature
In this study, the grain boundary character and texture of 50% and 90% cold-rolled FePd alloy was investigated during recrystallization at 700 °C. Electron backscatter diffraction (EBSD) measurements were performed on the rolling direction to normal direction section. Kernel average misorientation (KAM) calculated from EBSD measurements was employed to determine the recrystallization fraction. ...
متن کاملThe influence of microchemistry on the recrystallization texture of cold-rolled Al-Mn-Fe-Si alloys
The recrystallization textures of a cold-rolled Al-Mn-Fe-Si model alloy with three different microchemistry states after non-isothermal annealing were studied. The microstructure and texture evolution have been characterized by EBSD. It is clearly demonstrated that the actual microchemistry state as determined by the homogenization procedure strongly influence the recrystallized grain size and ...
متن کاملMicrostructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
متن کاملKinetics of individual grains during recrystallization of cold-rolled copper
The formation of a recrystallization texture is closely related to the nucleation and growth of recrystallizing grains, which may vary from grain to grain. Cube texture is a commonly observed recrystallization texture in face centered cubic metals of medium to high stacking fault energy after heavy cold-rolling and annealing. In this work, recrystallization of pure copper cold-rolled to a von M...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1959
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.23.6_343