Recrystallization of Cold-Rolled Sintered Aluminum Products (S.A.P.)
نویسندگان
چکیده
منابع مشابه
Recrystallization and Texture Development in Hot Rolled 1050 Aluminum
The evolution of texture as a function of recrystallization has been characterized for hotrolled AA1050. Samples prepared from hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The microstructural variation and texture evolution in the samples was observed by automatic indexing of Electron Back Scatter Diffraction (EBSD) patterns in a Scanning ...
متن کاملMicrostructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
متن کاملKinetics of individual grains during recrystallization of cold-rolled copper
The formation of a recrystallization texture is closely related to the nucleation and growth of recrystallizing grains, which may vary from grain to grain. Cube texture is a commonly observed recrystallization texture in face centered cubic metals of medium to high stacking fault energy after heavy cold-rolling and annealing. In this work, recrystallization of pure copper cold-rolled to a von M...
متن کاملKinetics of Austenite Recrystallization during the Annealing of Cold-rolled Fe-Mn-Al-C Steel
In the current study, the recrystallization behavior of 75% cold-rolled Fe-22Mn-10Al-1.4C steel during annealing at 750, 770, 790, 810, and 830°C was studied. X-ray diffraction patterns and optical microscopy were used to characterize microstructures. The Vickers Micro-hardness test was used to characterize recrystallization kinetics during annealing. Johnson-Mehl-Avrami-Kolmogorov (JMAK) model...
متن کاملEvolution of microstructure and texture during recovery and recrystallization in heavily rolled aluminum
The annealing behavior of nanostructured aluminum AA1050 prepared by cold rolling to an ultrahigh strain (vM = 6.4) has been investigated using both transmission electron microscopy and electron backscatter diffraction techniques, paying particular attention to changes in microstructure and texture during recovery and their influence on subsequent recrystallization. It is found that coarsening...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Institute of Metals and Materials
سال: 1966
ISSN: 0021-4876,1880-6880
DOI: 10.2320/jinstmet1952.30.9_811