Recrystallization behavior during hot rolling of 3004 aluminum alloy.
نویسندگان
چکیده
منابع مشابه
Microstructural evolution during recrystallization in hot rolled Aluminum Alloy 1050
The evolution of texture as a function of recrystallization has been characterized for hot-rolled AA1050. Samples prepared from a hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The spatial orientation variation within the deformed microstructure of nucleation, growth and orientations of recrystallized grains is examined. The microstructural ...
متن کاملEffect of Composition on the Recrystallization Behavior of if Steels During Simulated Hot Strip Rolling
Flow curves are generated in muti-pass torsion tests for a titanium stabilized and a niobium stabilized IF steel. Two types of test schedule are used, one based on plate rolling and the other approximating strip rolling. The purpose of the former is to define the three critical temperatures of steel rolling. The strip schedules are varied in order to investigate the influence of increasing the ...
متن کاملIn situ study of dynamic recrystallization and hot deformation behavior of a multiphase titanium aluminide alloy
multiphase titanium aluminide alloy Klaus-Dieter Liss, Thomas Schmoelzer, Kun Yan, Mark Reid, Matthew Peel, Rian Dippenaar, and Helmut Clemens Australian Nuclear Science and Technology Organisation, PMB 1, Menai, New South Wales 2234, Australia Department of Physical Metallurgy and Materials Testing, Montanuniversität, A-8700 Leoben, Austria Faculty of Engineering, University of Wollongong, Wol...
متن کاملRheological behavior of a commercial AA5182 aluminum alloy during solidification
During casting of aluminum alloys, the partially solidified material is submitted to thermally induced strains that can lead to severe casting defects, such as hot tearing. In this work, carried out in the frame of the European project VIR[CAST], the rheological behavior of a partially solidified AA5182 aluminum alloy has been investigated in order to provide constitutive equations to predict h...
متن کاملRecrystallization and Texture Development in Hot Rolled 1050 Aluminum
The evolution of texture as a function of recrystallization has been characterized for hotrolled AA1050. Samples prepared from hot rolled sheet were annealed isothermally for sufficient time to allow complete recrystallization. The microstructural variation and texture evolution in the samples was observed by automatic indexing of Electron Back Scatter Diffraction (EBSD) patterns in a Scanning ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Japan Institute of Light Metals
سال: 1989
ISSN: 0451-5994
DOI: 10.2464/jilm.39.94