Realizing Ultrafine Grained Steel by Simple Hot Deformation Using Dynamic Transformation and Subsequent Dynamic Recrystallization Mechanisms
نویسندگان
چکیده
منابع مشابه
Combination of dynamic transformation and dynamic recrystallization for realizing ultrafine-grained steels with superior mechanical properties
Dynamic recrystallization (DRX) is an important grain refinement mechanism to fabricate steels with high strength and high ductility (toughness). The conventional DRX mechanism has reached the limitation of refining grains to several microns even though employing high-strain deformation. Here we show a DRX phenomenon occurring in the dynamically transformed (DT) ferrite, by which the required s...
متن کاملDynamic Recrystallization under Hot Deformation of a PH Stainless Steel
Dynamic recrystallization, DRX, behaviour of a precipitation hardened, PH, stainless steel was studied in connection with microstructural developments in a compression test. The experimental results showed that the dominant mechanism of softening is DRX, but at high strain rates and low temperatures, ie, high Zener-Holman parameter, Z, work hardening and dynamic recovery, DRV, produced a pancke...
متن کاملDynamic Recrystallization by Necklace Mechanism During Hot Deformation of 316 Stainless Steel
The aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (DRX). The material used is 316 stainless steel. In order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of 950-1100 °C with strain rates of 0.01-1s-1. The result shows that at the tempera...
متن کاملdynamic recrystallization under hot deformation of a ph stainless steel
dynamic recrystallization, drx, behaviour of a precipitation hardened, ph, stainless steel was studied in connection with microstructural developments in a compression test. the experimental results showed that the dominant mechanism of softening is drx, but at high strain rates and low temperatures, ie, high zener-holman parameter, z, work hardening and dynamic recovery, drv, produced a pancke...
متن کاملdynamic recrystallization by necklace mechanism during hot deformation of 316 stainless steel
the aim of this study is to investigate the nucleation of new grains by necklacing mechanism during dynamic recrystallization (drx). the material used is 316 stainless steel. in order to modeling the deformation behavior during hot rolling, one-hit compression tests were performed at temperature range of 950-1100 °c with strain rates of 0.01-1s-1. the result shows that at the temperature of 100...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOP Conference Series: Materials Science and Engineering
سال: 2017
ISSN: 1757-8981,1757-899X
DOI: 10.1088/1757-899x/194/1/012026