Reactive Infiltration Processing and Secondary Compressive Creep of NiAl and NiAl-W Composites
Reactive infiltration processing was used to fabricate bulk NiAl and fiber-reinforced NiAl composites. Homogenous, pore-free materials were obtained by chemical reaction between nickel and aluminum after complete infiltration with liquid aluminum of preforms of nickel wires (containing tungsten wires for the composites) with low surface-to-volume ratio, high permeability, and regular infiltrati...
متن کاملReactive Infiltration Processing and Compression Creep of NiAl and NiAl Composites
....................................... 2 TA BLE O F C O N TEN TS ................................................................................................. ..................................... 3 LIST OF FIGURES .................................. ............................... ....... ......................... 5 LIST O F T A B LE S .........................................................
متن کاملTensile Creep of Polycrystalline Near-Stoichiometric NiAl
Long term tensile creep studies were conducted on binary NiAl in the temperature range 700-1200 K with the objectives of characterizing and understanding the creep mechanisms. Inverse and normal primary creep curves were observed depending on stress and temperature. It is concluded that the primary creep of NiAl is limited by dislocation mobility. The stress exponent for creep, n, decreased fro...
متن کاملMeasurement and Modeling of Creep in Open-Cell NiAl Foams
Nickel-rich NiAl foams, consisting of open cells with hollow struts and exhibiting two relative densities (5.0 and 6.6 pct) and average cell sizes (1.27 and 0.85 mm), were creep tested between 800 °C and 1100 °C under compressive stresses between 0.10 and 1.50 MPa. For stresses lower than 0.50 MPa, the foams exhibit secondary creep with power-law behavior characterized by creep exponents and ac...
متن کاملEFFECT OF NICKEL AND COBALT ADDITIONS ON INFILTRATION BEHAVIOR, MICROSTRUCTURE AND HARDNESS OF W-AG COMPOSITES
In this research, infiltration behavior of W-Ag composite compacts with Nickel and Cobalt as additives has been investigated. Nickel and Cobalt were added to Tungsten powder by two distinct methods: mixing elementally and reduction of salt solution. The coated Tungsten powders were compacted under controlled pressures to make porous skeleton with 32-37 vol. % porosity. Infiltration process was ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Metallurgical and Materials Transactions A
سال: 2000
ISSN: 1073-5623,1543-1940
DOI: 10.1007/s11661-000-0020-7