RATIONALE FOR CONTROLLED COOLING PARAMETERS HIGH CARBON ROLLED STEEL IN WIRE MILL STREAM 320/150 JSC «MSW»
نویسندگان
چکیده
منابع مشابه
Developing Very Fine Nanopearlitic Structure in a High Carbon Steel Wire before Drawing
The effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. In this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. The results were the minimum interlamellar spacing of 35 nm and maximum ulti...
متن کاملThe Effect on Rolling Mill of Waviness in Hot Rolled Steel
The edge waviness in hot rolled steel is a common defect. Variables that affect such defect include raw material and machine. These variables are necessary to consider to understand such defect. This research studied the defect of edge waviness for SS 400 of metal sheet manufacture. Defect of metal sheets were divided into two groups. The specimens were investigated on chemical composition and ...
متن کاملStatic Strain Aging Behavior of Low Carbon Steel Drawn Wire
The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...
متن کاملdeveloping very fine nanopearlitic structure in a high carbon steel wire before drawing
the effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. in this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. the results were the minimum interlamellar spacing of 35 nm and maximum ulti...
متن کاملThe Effect of Multiple Bending of Wire on the Residual Stresses of High Carbon Steel Wires
R. Kruzel, M. Suliga, Czestochowa University of Technology, Czestochowa, Poland Steel tire cord, springs and rope wires belong to the group of metal products from which the low residual stresses are required. In this paper the eff ect of multiple bending of wire on residual stresses of high carbon steel wires has been assessed. It was found that the application of the multi-roller straightening...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Mechanical Engineering the National Technical University of Ukraine "Kyiv Polytechnic Institute"
سال: 2016
ISSN: 2409-5966,2305-9001
DOI: 10.20535/2305-9001.2016.77.73756