Radiation-Induced Demagnetization of Nd-Fe-B Permanent Magnets
Introduction The Advanced Photon Source (APS), as well as other third-generation synchrotron light sources, uses permanent magnets in the insertion devices to produce x-rays for scientific research [1,2]. When placed in a high-energy storage ring, these permanent magnets are subjected to irradiation from synchrotron radiation, high-energy bremsstrahlung, and bremsstrahlung-produced neutrons. Pr...
متن کاملImpulse Magnetization of Nd-Fe-B Sintered Magnets for Sensors
Magnetization of large Nd-Fe-B sintered permanent magnets is still challenging. This type of permanent magnet is electrically conductive, so impulse magnetization causes a flow of eddy currents which prevent magnetization of the whole volume of the magnet. The paper deals with the impulse magnetization of sintered Nd-Fe-B permanent magnets and shows a method for the determination of suitable pa...
متن کاملSintering of Nd-Fe-B Magnets from Dy Coated Powder
High-coercive (Nd,Dy)-Fe-B magnets were fabricated via dysprosium coating on Nd-Fe-B powder. The sputtering coating process of Nd–Fe–B powder yielded samples with densities greater than 98%. (Nd,Dy)2Fe14B phases may have effectively penetrated into the boundaries between neighboring Nd2Fe14B grains during the sputtering coating process, thereby forming a (Nd,Dy)2Fe14B phase at the grain boundar...
متن کاملHigh performance Nd-Fe-B permanent magnets without critical elements
Scanning electron microscopy, and magnetization measurements reveal that as cast (Nd1 xCex)2Fe14B alloys contain significant amounts of a-Fe that can be dramatically reduced by annealing the alloys at 1000 C for 3 days. The room temperature intrinsic coercivity, Hci, of (Nd0.8Ce0.2)2.2Fe14B melt spun ribbons was found to be 11 kOe, which is ~32e~10% higher in comparison to that of Nd2Fe14B (Hci...
متن کاملEffect of Post-Sintering Annealing Treatment on Magnetic Properties of Some Nd Fe b Based Magnets
Effects of post-sintering annealing treatment between 300 and 1000ºC for up to 8 hrs time periods followed by either furnace cooling (FC) or air-cooling (AC) on the hard magnetic properties of some Nd-Fe-B based sintered magnets was investigated. It was shown that the intrinsic coercivity (Hci), second quadrant demagnetization loop shape and thus the energy density (BH)max varied considerably a...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 1989
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.36.877