Rapid Heating Patenting of High Carbon Steel Wire Rods
نویسندگان
چکیده
منابع مشابه
Static Strain Aging Behavior of Low Carbon Steel Drawn Wire
The static strain aging is a phenomenon that can change the mechanical properties of low carbon steels. Thus, the static strain aging behavior of low carbon steel wires after drawing process is studied. To do so, the wires are austenitized at different temperatures and cooled in different rates. Then the wires are drawn and aged at a specific temperature and time. Before and after aging of each...
متن کاملDeveloping Very Fine Nanopearlitic Structure in a High Carbon Steel Wire before Drawing
The effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. In this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. The results were the minimum interlamellar spacing of 35 nm and maximum ulti...
متن کاملThe Effect of Multiple Bending of Wire on the Residual Stresses of High Carbon Steel Wires
R. Kruzel, M. Suliga, Czestochowa University of Technology, Czestochowa, Poland Steel tire cord, springs and rope wires belong to the group of metal products from which the low residual stresses are required. In this paper the eff ect of multiple bending of wire on residual stresses of high carbon steel wires has been assessed. It was found that the application of the multi-roller straightening...
متن کاملCarbon Wire Heating Due to Scattering in the Sns
In the SNS, the 2.5 MeV H beam from the RFQ will be accelerated in the Linac to 1 GeV, and then injected into the High Energy Beam Transport (HEBT). After passing through HEBT, the electrons are stripped during injection into the Accumulator Ring. The proton beam will be accumulated in the Ring for around 1000 turns before ejecting to the Ring to Target Beam Transport (RTBT). The filling time o...
متن کاملdeveloping very fine nanopearlitic structure in a high carbon steel wire before drawing
the effects of steel wire patenting process parameters on very fine interlamellar spacing in the pearlitic steel wire were investigated and the optimized condition of the process was achieved. in this work, the initial nanopearlitic structure was obtained in a 0.72 wt% carbon steel wire before the wire drawing process. the results were the minimum interlamellar spacing of 35 nm and maximum ulti...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Transactions of the Iron and Steel Institute of Japan
سال: 1977
ISSN: 0021-1583,1881-1183
DOI: 10.2355/isijinternational1966.17.359