Quantification of stress-induced damage and post-fire response of 5083 aluminum alloy

Friction stir welding of dissimilar joint of aluminum alloy 5083 and commercially pure titanium

In this study, commercially pure titanium and aluminum alloy 5083 in connection rotational speed of 1120 rpm and a feed rate of 50 mm per minute for butt welding by friction stir welding has been successfully completed. Micro-structure, hardness and tensile test was conducted on the connection. Welding area is a composite of aluminum and titanium particles that the particles plays an important ...

Friction stir welding of dissimilar joint of aluminum alloy 5083 and commercially pure titanium

In this study, commercially pure titanium and aluminum alloy 5083 in connection rotational speed of 1120 rpm and a feed rate of 50 mm per minute for butt welding by friction stir welding has been successfully completed. Micro-structure, hardness and tensile test was conducted on the connection. Welding area is a composite of aluminum and titanium particles that the particles plays an important ...

Effect of welding parameters on penetration depth in FB-TIG welding of 5083 aluminum alloy

In the present study, effect of current, welding speed and preheat temperature during FB-TIG welding of AA5083 aluminum alloy was studied. Using the Taguchi method, 9 different tests were designed to investigate the effect of welding parameters on the penetration depth. Consistent with predictions, increasing the current and preheat temperature, and reducing the welding speed led to an increase...

Effect of welding parameters on penetration depth in FB-TIG welding of 5083 aluminum alloy

In the present study, effect of current, welding speed and preheat temperature during FB-TIG welding of AA5083 aluminum alloy was studied. Using the Taguchi method, 9 different tests were designed to investigate the effect of welding parameters on the penetration depth. Consistent with predictions, increasing the current and preheat temperature, and reducing the welding speed led to an increase...

Characterization of Nanocrystalline Aluminum Alloy 5083 Powders Produced by Cryogenic Attrition