Comparative Evaluation of Push-Out Bond Strength Of Calcium Silicate Based Materials: An Ex-Vivo Study
Materials and Methods: 15 single rooted premolars were selected and middle portion of each root was sectioned perpendicular to the long axis to produce two discs of 2.00 ± 0.05 mm thickness using a diamond disk. 30 root slices were produced and canal lumen was widened using Gates Glidden drills to produce standardized internal diameter of 1.3mm and root sections were filled with ERRM, MTA and B...
متن کاملPush-out bond strength of intra-orifice barrier materials: Bulk- fill composite versus calcium silicate cement
Background. The aim of this study was to compare the push-out bond strengths of calcium silicate-based ProRoot MTA and Biodentine cements and SureFil SDR and EverX Posterior bulk-fill composite resins. Methods. Twenty-four single-rooted maxillary central incisors were sectioned below the cementoenamel junction, and the root canals were instrumented using rotary files. Thereafter, a parallel pos...
متن کاملeffect of blood exposure on push-out bond strength of four calcium silicate based cements
introduction: the purpose of this study was to compare the push-out bond strength of white proroot mineral trioxide aggregate (mta), biodentine, calcium-enriched mixture (cem) cement and endosequence root repair material (errm) putty after exposure to blood. methods and materials: a total of 96 root dentin slices with a standardized thickness of 1.00±0.05 mm and standardized canal spaces were r...
متن کاملEffect of Blood Exposure on Push-Out Bond Strength of Four Calcium Silicate Based Cements
INTRODUCTION The purpose of this study was to compare the push-out bond strength of white ProRoot Mineral Trioxide Aggregate (MTA), Biodentine, calcium-enriched mixture (CEM) cement and Endosequence Root Repair Material (ERRM) putty after exposure to blood. METHODS AND MATERIALS A total of 96 root dentin slices with a standardized thickness of 1.00±0.05 mm and standardized canal spaces were r...
متن کاملPush-out bond strength of MTA HP, a new high-plasticity calcium silicate-based cement.
This study was designed to investigate the resistance to dislodgment provided by MTA HP, a new high-plasticity calcium silicate-based cement. Biodentine and White MTA Angelus were used as reference materials for comparison. Three discs 1 ± 0.1 mm thick were obtained from the middle third of the roots of 5 maxillary canines. Three 0.8-mm-wide holes were drilled on the axial surface of each root ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Medical Principles and Practice
سال: 2017
ISSN: 1011-7571,1423-0151
DOI: 10.1159/000477683