Pulsed Electrodeposition for Copper Nanowires
نویسندگان
چکیده
منابع مشابه
Pulsed Electrodeposition of Copper
Pulsed electrolysis of copper has been systematically investigated by electrodepositing copper from a copper sulfate bath. Pulse duty cycles of 5 to 80 percent, at frequencies from 10 to 100 Hz with current densities ranging from 2.5 to 7.5 A/dm2 were employed. The appearance of Hull Cell panels with both direct current and pulsed current was recorded. The influence of pulsed current on current...
متن کاملThe effect of pulsed electrodeposition parameters on the microstructure and magnetic properties of the CoNi nanowires
CoNi nanowires were deposited by pulsed electrodeposition technique into porous alumina templates. The effect of off time between pulses (toff) and reductive/oxidative time (treduc/oxid) on the microstructure and magnetic properties of the CoNi nanowires were investigated. Maximum coercivity and squareness were obtained for samples fabricated at treduc/oxid= 0.5 ms and toff =400 ms. The coerciv...
متن کاملMolybdenum nanowires by electrodeposition.
Metallic molybdenum (Mo(o)) wires with diameters ranging from 15 nanometers to 1.0 micrometers and lengths of up to 500 micrometers (0.5 millimeters) were prepared in a two-step procedure. Molybdenum oxide wires were electrodeposited selectively at step edges and then reduced in hydrogen gas at 500 degrees C to yield Mo(o). The hemicylindrical wires prepared by this technique were self-uniform,...
متن کاملElectrodeposition of Thermoelectric Superlattice Nanowires
There is a renewed interest in the field of thermoelectrics because of the remarkable efficiency improvement that can be achieved in nanostructured materials, for example, superlattice thin films and quantum dots. Theoretical calculations predict that further enhancement of the thermoelectric figure of merit can be achieved in superlattice nanowires (zero-dimensional) [5] rather than convention...
متن کاملthe effect of pulsed electrodeposition parameters on the microstructure and magnetic properties of the coni nanowires
coni nanowires were deposited by pulsed electrodeposition technique into porous alumina templates. the effect of off time between pulses (toff) and reductive/oxidative time (treduc/oxid) on the microstructure and magnetic properties of the coni nanowires were investigated. maximum coercivity and squareness were obtained for samples fabricated at treduc/oxid= 0.5 ms and toff =400 ms. the coerciv...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Crystals
سال: 2020
ISSN: 2073-4352
DOI: 10.3390/cryst10030218