Prospect of Life Prediction in Long-Term Fatigue, Creep and Creep-Fatigue for Components Operated at Elevated Temperatures
نویسندگان
چکیده
منابع مشابه
The Fracture Mechanics Concept of Creep and Creep/Fatigue Crack Growth in Life Assessment
There is an increasing need to assess the service life of components containing defect which operate at high temperature. This paper describes the current fracture mechanics concepts that are employed to predict cracking of engineering materials at high temperatures under static and cyclic loading. The relationship between these concepts and those of high temperature life assessment methods is ...
متن کاملLifetime prediction in creep-fatigue environment
The creep-fatigue interaction has been studied and innovative mathematical models are proposed to predict the operating life of aircraft components, specifically gas turbine blades subject to creep-fatigue at high temperatures. The historical evolution of the creep-fatigue lifetime prediction is given in order to place the present study in the context. A literature review of the life estimation...
متن کاملCreep-Fatigue Failure Diagnosis
Failure diagnosis invariably involves consideration of both associated material condition and the results of a mechanical analysis of prior operating history. This Review focuses on these aspects with particular reference to creep-fatigue failure diagnosis. Creep-fatigue cracking can be due to a spectrum of loading conditions ranging from pure cyclic to mainly steady loading with infrequent off...
متن کاملA Novel Viscosity-Based Model for Low Cycle Fatigue Creep Life Prediction of High-Temperature Structures
Damage evolution during low cycle fatigue, creep, and their interaction behavior is actually a ductility exhaustion process in response to cyclic and static creep. In this article, a novel viscosity-based model for low cycle fatigue creep life prediction is presented in an attempt to condition viscosity-based approaches for general use in isothermal and thermo-mechanical loading. In this model,...
متن کاملAn efficient life prediction methodology for low cycle fatigue–creep based on ductility exhaustion theory
Low cycle fatigue–creep is the main reason for the failures of many engineering components under high temperature and cyclic loading. Based on the exhaustion of the static toughness and dissipation of the plastic strain energy during fatigue failure, a new low cycle fatigue–creep life prediction model that is consistent with the fatigue–creep damage mechanism and sensitive to the fatigue damage...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Society of Materials Science, Japan
سال: 2015
ISSN: 0514-5163,1880-7488
DOI: 10.2472/jsms.64.65