Properties of Wood Ceramics Prepared from Thermo-Modified Poplar
نویسندگان
چکیده
منابع مشابه
Preparation of Modified Beeswax and Its Influence on the Surface Properties of Compressed Poplar Wood
Beeswax was modified through the direct blending of nano-TiO₂, chitosan, acid dyes, and neutral dyes. With the varied modified beeswax, hot waxing was conducted on compressed poplar wood. Treated wood surfaces were characterized with scanning electron microscopy and thermogravimetric analysis. Results show that the C, O, N, Au, S, and Ti elements in modified beeswax successfully penetrated into...
متن کاملthermal properties of wood-plastic composites prepared from hemicellulose-extracted wood flour
hemicellulose of southern yellow pine wood spices was extracted by pressurized hot water at three different temperatures: 140°c, 155°c and 170°c. compounding with pp (polypropylene) was performed by extrusion after preparing wood flour and sieving to determine its mesh size. the ratio of wood to polymer was 50:50 based on oven-dry weight of wood flour. all extraction treatments and control samp...
متن کاملStructural and other properties of modified wood
Wood is not under all circumstances an appropriate building material. Beside others, structural properties and biological durability determine the limits for the use of wood. Until recently, the only industrial applied method to improve the durability of wood was impregnating with toxic wood preservatives. Although much progress has been made in improving the fixation of preservatives (i.e. emi...
متن کاملPorous Ba Ferrite Prepared from Wood Template
Ba ferrite materials with porous microstructures were prepared from a natural cedar wood template in order to investigate new electromagnetic shielding materials. The wood templates were infiltrated with barium nitrate and iron nitrate solutions (molar ratio = 1:12) and dried to form ferrite gel, then, they were sintered in air at a temperature between 800 °C and 1400 °C. The 1-dimensional poro...
متن کاملInvestigation of the Creep Property of Fast-growing Poplar Wood Modified with Low Molecular Weight Resins
Fast-growing poplar wood was modified with low molecular weight ureaformaldehyde resin (UF) at 41.5% concentration or phenol-formaldehyde (PF) at concentrations of 15, 25, and 40%. The physical and mechanical properties were measured, and creep behavior tests were carried out under ambient indoor conditions. The specimens were subjected to 30 and 50% of their maximum bending load. The density, ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Forests
سال: 2020
ISSN: 1999-4907
DOI: 10.3390/f11111204