Properties evaluation of silorane, low-shrinkage, non-flowable and flowable resin-based composites in dentistry
نویسندگان
چکیده
منابع مشابه
Properties evaluation of silorane, low-shrinkage, non-flowable and flowable resin-based composites in dentistry
Purpose. This study tested the null hypothesis that different classes of direct restorative dental materials: silorane-based resin, low-shrinkage and conventional (non-flowable and flowable) resin-based composite (RBC) do not differ from each other with regard to polymerization shrinkage, depth of cure or microhardness. Methods. 140 RBC samples were fabricated and tested by one calibrated opera...
متن کاملDynamic thermo-mechanical properties of various flowable resin composites
BACKGROUND This study compared the storage modulus (E'), the loss modulus (E'') and the loss tangent (tan δ) of various flowable resin composites. MATERIAL AND METHODS Grandio Flow (GRF), GrandioSo Heavy Flow (GHF), Filtek Supreme XTE (XTE) and Filtek Bulk Fill (BUL) flowable resins and Clinpro Sealant (CLI) ultra-flowable pit and fissure sealant resin were used. 25 samples were tested using ...
متن کاملMarginal gap repair with flowable resin-based composites.
This study was designed to test the hypothesis that the flowable/dentin interface has the weakest bond and highest frequency of failure when a resin-based composite is repaired using a flowable composite. Comparing three specific groups--dentin, flowable composite, and hybrid composite-under the Kruskal-Wallis test showed that the mean bond strength values at the flowable/dentin interface and w...
متن کاملShrinkage behaviour of flowable resin-composites related to conversion and filler-fraction.
OBJECTIVES To evaluate the shrinkage-strain, degree of conversion (DC) and percent filler of a range of flowable resin-composites. METHODS Several commercially available flowable resin-composites were selected. The bonded-disk technique was used to measure shrinkage-strain kinetics. Measurements were obtained continuously for 60min by irradiation for 40s at 750mW/cm(2) at two initial temperat...
متن کاملSilorane- and high filled-based "low-shrinkage" resin composites: shrinkage, flexural strength and modulus.
This study compared the volumetric shrinkage (VS), flexural strength (FS) and flexural modulus (FM) properties of the low-shrinkage resin composite Aelite LS (Bisco) to those of Filtek LS (3M ESPE) and two regular dimethacrylate-based resin composites, the microfilled Heliomolar (Ivoclar Vivadent) and the microhybrid Aelite Universal (Bisco). The composites (n = 5) were placed on the Teflon ped...