Progress on Hydrothermal Stability of Dental Zirconia Ceramics

Surface roughened zirconia: towards hydrothermal stability.

Surface roughness is needed in several yttria-stabilized zirconia components used in restorative dentistry for osseointegration or adhesion purposes. This can be achieved by different treatments, which may also modify the microstructure of the surface. Among them, sandblasting and chemical etching are widely used, but their effect on hydrothermal aging of zirconia is not fully understood. In th...

Comparative Study of Physical Properties of Zirconia Based Dental Ceramics

..........................................................................................................I Acknowledgements......................................................................................................II Table of

Long Term Fatigue Behavior of Zirconia Based Dental Ceramics

This study evaluated the influence of cyclic loading on zirconia bar-shaped specimens after being subjected to three different surface treatments: particle abrasion with either 50 μm or 110 μm alumina and grinding with diamond points, while polished specimens served as a control. Statistical analysis revealed significant reduction (38-67%) in flexure strength (P < 0.001) after three million cyc...

Processing and Properties of Zirconia Ceramics for Dental Applications

Low-temperature degradation of different zirconia ceramics for dental applications.

The aim of this investigation was to determine the influence of simulated ageing on the tetragonal-to-monoclinic phase transformation and on the flexural strength of a 3Y-TZP ceramic, compared to alumina toughened zirconia (ATZ) and ceria-stabilized zirconia (12Ce-TZP). Standardized disc specimens of each material were hydrothermally aged in steam at 134°C and 3bar for 0, 16, 32, 64 or 128h. Th...