PRODUCTION AND CHARACTERIZATION OF ALUMINA NANOPARTICLES FROM GIRO CLAY VIA ACID LEACHING WITH SOL GEL METHOD
نویسندگان
چکیده
منابع مشابه
Preparation and Characterization of High Specific Surface Area γ-Alumina Nanoparticles Via Sol-Gel Method
In the present investigation, γ-alumina nanoparticles with particle sizes less than 10 nm, high specific surface area (351 m2/g), high pore volumes and relatively narrow pore sizes distribution was prepared via sol-gel method in presence of aluminum isopropoxide as an aluminum precursor, distilled water, acetic acid as hydrolysis rate controller and tert-butanol as solvent. They had meso ...
متن کاملSonosynthesis and characterization of nano ZnO/Montmorillonite nano clay composite via Sol-Gel method
Nano ZnO/ montmorillonite composite were prepared by sol gel method under ultrasonic irradiation from directly mixing montmorillonite nano clay into Zinc gel. The Zn(CH3COO)2.2H2O and montmorillonite nano clay was used as precursor. The zinc acetate was dissolved in DI water and, NH3 (aq) solution was dropped into the zinc solution until pH 9 consequently the zinc gel was produced. The montmori...
متن کاملSonosynthesis and characterization of nano ZnO/Montmorillonite nano clay composite via Sol-Gel method
Nano ZnO/ montmorillonite composite were prepared by sol gel method under ultrasonic irradiation from directly mixing montmorillonite nano clay into Zinc gel. The Zn(CH3COO)2.2H2O and montmorillonite nano clay was used as precursor. The zinc acetate was dissolved in DI water and, NH3 (aq) solution was dropped into the zinc solution until pH 9 consequently the zinc gel was produced. The montmori...
متن کاملSynthesis and characterization of Alumina (Al2O3) nanoparticles prepared by simple sol-gel method
Alumina is one of the most widely used ceramic materials as catalysts, catalyst supports and absorbents, and also wear resistant coating. This study focused on fabricating and characterizing of alumina ceramic nanoparticles fabricated using new and simple sol-gel method. Aluminium oxide (Al2O3) nanoparticles were synthesized by iron (III) nitrate 9-hydrate as precursor. Physicochemical properti...
متن کاملSynthesis and characterization of Alumina (Al2O3) nanoparticles prepared by simple sol-gel method
Alumina is one of the most widely used ceramic materials as catalysts, catalyst supports and absorbents, and also wear resistant coating. This study focused on fabricating and characterizing of alumina ceramic nanoparticles fabricated using new and simple sol-gel method. Aluminium oxide (Al2O3) nanoparticles were synthesized by iron (III) nitrate 9-hydrate as precursor. Physicochemical properti...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: FUTA JOURNAL OF ENGINEERING AND ENGINEERING TECHNOLOGY
سال: 2021
ISSN: 2636-6045,2636-6045
DOI: 10.51459/futajeet.2021.15.1.261