Probabilistic fatigue crack growth assessment of Al 7075-T6 aerospace component
نویسندگان
چکیده
منابع مشابه
Ionic Inhibition of Environmental Fatigue Crack Growth in 7075-t6
The objective of this study is to quantify and understand the effectiveness of a hexavalent chrome replacement ion to inhibit environmentally assisted fatigue crack propagation (EFCP) in high strength aluminum alloys. Because of dynamic-cyclic stress (or strain) loading, fatigue degradation occurs at stress levels considerably lower than the tensile or yield strength; degradation is exacerbated...
متن کاملتضعیف امواج آکوستیک در Al 7075-T6 و St 304
Propagation and dispersion of acoustic waves is one of the important phenomena in physics. Acoustic-waves are nowadays widely used in a variety of applications ranging from underwater communications, identification and specification of the internal defects of materials to extracorporeal shock wave lithotripsy. Apart from application and utilization of such phenomena, study on production and pro...
متن کاملProbabilistic Prognosis of Non-Planar Fatigue Crack Growth
Quantifying the uncertainty in model parameters for the purpose of damage prognosis can be accomplished utilizing Bayesian inference and damage diagnosis techniques such as non-destructive evaluation or structural health monitoring. The number of samples required to solve the Bayesian inverse problem through common sampling techniques (e.g., Markov chain Monte Carlo) renders high-fidelity finit...
متن کاملEnhanced Exponential Fatigue Crack Growth Model for Al-alloy
In the present investigation, an attempt has been made to use “exponential model” in the prediction of fatigue life without integrating the fatigue crack growth rate curve (FCGR). The obtained results are compared with experimental crack growth data obtained for 2024-T351 aluminum alloy for four bending V-Charpy specimens under constant amplitude loading in stress ratio range from 0.1 to 0.3 an...
متن کاملThe Fracture Mechanics Concept of Creep and Creep/Fatigue Crack Growth in Life Assessment
There is an increasing need to assess the service life of components containing defect which operate at high temperature. This paper describes the current fracture mechanics concepts that are employed to predict cracking of engineering materials at high temperatures under static and cyclic loading. The relationship between these concepts and those of high temperature life assessment methods is ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Procedia Structural Integrity
سال: 2017
ISSN: 2452-3216
DOI: 10.1016/j.prostr.2017.07.192