Press Formability of Half-alloyed Galvanized Steel.
نویسندگان
چکیده
منابع مشابه
Corrosion of Galvanized Steel in Soils
The results of measurements of the corrosion of galvanized steel and of bare steel and zinc as reference materials after exposure to different soil conditions for a maximum of 13 years are reported. The magnitude and progress of corrosion of galvanized steel as determined by weight loss and pitting is interpreted in terms of the environmental conditions to which the specimens were exposed. From...
متن کاملDevelopment of Niobium Alloyed Press Hardening Steel with Improved Properties for Crash Performance
Press hardening steel has become a much used material in car body manufacturing due to its excellent safety and lightweight potential. In some recent car models press hardening steel has reached already a weight share of more than 20% in the body structure while it is estimated that it could reach even around 40% in the future. However conventional press hardening steel based on the alloying co...
متن کاملThe way forward in passivation of galvanized steel coils
Within the Fives Group, Fives Stein, Fives DMS and Fives Bronx design and supply a wide range of production, transformation and treatment lines for carbon, stainless and silicon steel. From pickling and annealing lines to the continuous galvanizing line, from rolling mills to tube and pipe mills, our teams will offer you their expertise and the best available technologies to achieve the highest...
متن کاملEffect of Laser Welding on Formability of DP980 steel
Limiting dome height (LDH) tests were used to evaluate the formability of laser butt welded blanks of the dual phase 980 steel in comparison with the base metal. Two different lasers were used: diode and Nd:YAG, giving a wide range of welding thermal cycles. A sharp decrease in LDH was observed in the welded specimens due to the formation of a softened zone in the outer heat affected zone. Soft...
متن کاملStudies on defects in galvanized coating on steel wire
Causes for deposition of defective galvanized coating (lumpy deposition of coating during hot dip galvanizing) of carbon-steel wire have been investigated. It is established that the lumpy deposition is caused due to segregation of silicon on the surface of steel wire. Due to this change in composition of the steel at surface, the regions get modified and lie in Sandelin hyper reactive zone. Th...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Surface Finishing Society of Japan
سال: 1996
ISSN: 0915-1869,1884-3409
DOI: 10.4139/sfj.47.696