Preparation of ZrB<sub>2</sub> Fine Powders Using Thermite Method by Reduction with Mg
نویسندگان
چکیده
منابع مشابه
Synthesis of HfB2 Powders by Carbothermal Reduction
In this research, solid state carbothermal synthesis of HfB2 Nano powders was investigated. For this purpose, HfO2,H3BO3, carbon active or phenolic resin were used as raw materials for carbothermal reaction. After 2-4 hours of milling the raw materials by a planetary ball in an ethanol media, the mixture was heat dried and pressed in to disks under pressure of 20-30 bar. The disks were then pla...
متن کاملPREPARATION AND SINTERING OF W-20%Wt Cu COMPOSITE POWDERS PRODUCED BY CO-PRECIPITATION METHOD
Abstract: materials can be fabricated by sintering of W-Cu composite powders. In this research W-20%wt Cu composite powderswas synthesized via a co-precipitation method. Precipitate obtained from a mixture of copper nitrate and ammoniumparatungstate (APT) in distilled water contained W-Cu compounds. This precipitate was washed, dried and calcinedat 550 of dried precipitate powder was determined...
متن کاملbuckling of viscoelastic composite plates using the finite strip method
در سال های اخیر، تقاضای استفاده از تئوری خطی ویسکوالاستیسیته بیشتر شده است. با افزایش استفاده از کامپوزیت های پیشرفته در صنایع هوایی و همچنین استفاده روزافزون از مواد پلیمری، اهمیت روش های دقیق طراحی و تحلیل چنین ساختارهایی بیشتر شده است. این مواد جدید از خودشان رفتارهای مکانیکی ارائه می دهند که با تئوری های الاستیسیته و ویسکوزیته، نمی توان آن ها را توصیف کرد. این مواد، خواص ویسکوالاستیک دارند....
Sonochemical Green Method for Preparation of Mg-Doped ZnO Nanostructures in Water with Enhanced Photocatalytic Activity
In this work, Mg-doped ZnO nanostructures were prepared in water under ultrasonic irradiation for 60 min without using any organic compounds or post preparation treatments. The prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive analysis of X-ray (EDX), diffuse reflectance spectroscopy (DRS...
متن کاملSynthesis of Mg(B1−xCx)2 Powders
We have synthesized bulk Mg(B1−xCx)2 from a mixture of elemental Mg, B, and the binary compound B4C. Carbon incorporation was dramatically improved by a two step reaction process at an elevated temperature of 1200 C. This reaction process results in a solubility limit near x∼0.07. We found that impurities in the starting B cause an additive suppression of Tc. We combine these data with Tc and H...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Ceramic Society of Japan
سال: 1992
ISSN: 0914-5400,1882-1022
DOI: 10.2109/jcersj.100.172