Preparation of ZrB2-ZrC-SiC-ZrO2 nanopowders with in-situ grown homogeneously dispersed SiC nanowires
نویسندگان
چکیده
منابع مشابه
The ZrO2 Formation in ZrB2/SiC Composite Irradiated by Laser
In order to clearly understand the details of ZrO₂ formation during ablation, high intensity continuous laser was chosen to irradiate ZrB₂/SiC. The results reveal that there are two different modes of ZrO₂ formation depending on whether liquid SiO₂ is present. When liquid SiO₂ is present, ZrO₂ generated by the oxidation of ZrB₂ is firstly dissolved into SiO₂. Then, ZrO₂ will precipitate again, ...
متن کاملسنتز و بررسی خواص نانو پودرکامپوزیتی ZrC-ZrB2-SiC
In this research, ZrC-ZrB2-SiC nanocomposite powder was synthesized by carbothermal and borocarbotermal reduction methods. Zirconium silicate was first milled for four hours Then eight mixtures of raw materials were prepared. Finally, the samples were pyrolyzed at 800 ° C for two hours and then heat-treated at 1500 ° C for 30 minutes under an argon atmosphere. X-ray diffraction (XRD) and scanni...
متن کاملFabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
متن کاملMethane combustion over Pd/ZrO2/SiC, Pd/CeO2/SiC, and Pd/Zr0.5Ce0.5O2/SiC catalysts
The performances of different promoters (CeO2, ZrO2 and Ce0.5Zr0.5O2 solid solution) modified Pd/SiC catalysts for methane combustion are studied. XRD and XPS results showed that Zr 4+ could be incorporated into the CeO2 lattice to form Zr0.5Ce0.5O2 solid solution. The catalytic activities of Pd/CeO2/SiC and Pd/ZrO2/SiC are lower than that of Pd/Zr0.5Ce0.5O2/SiC. The Pd/Zr0.5Ce0.5O2/SiC catalys...
متن کاملThe Effect of the Mg Content on Mechanosynthesis of ZrB2–SiC–ZrC Composite in the Mg/ZrSiO4/B2O3/C System
The influence of magnesium content on the mechanosynthesis of ZrB2–SiC–ZrC composite in Mg/ZrSiO4/B2O3/C mixture was investigated. Thermodynamic evaluations revealed that the amount of Mg played a main role, thereby; the overall reaction enthalpy and adiabatic temperature (Tad) changed by variation of magnesium content. According to differential thermal analysis (DTA) results, after 45min milli...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials & Design
سال: 2020
ISSN: 0264-1275
DOI: 10.1016/j.matdes.2020.109186