Preparation of Trivalent Chromium Coating on 6063 Aluminum Alloy
نویسندگان
چکیده
منابع مشابه
Trivalent Chromium Conversion Coating for Corrosion Protection of Aluminum Surface
Corrosion is the degradation or deterioration of metal components due to a reaction with the environment. Chromate conversion coating is applied to passivate metallic surface to slow down (and prevent to some extent) corrosion process. Chromate conversion process uses chromium compounds including hexavalent chromium, which is toxic, carcinogenic and hazardous to human health and environment. He...
متن کاملEffect of Die Entry Angle on Extrusion Responses of Aluminum 6063 Alloy
Mechanical properties response of extruded 6063 aluminum alloy at varied die entry angle has been investigated. Plain carbon and tool steel dies with entry angles of 15, 30, 45, 60, 75 and 90 were simulated. Extrusion on the alloy was done at ambient temperature (37C) and the extruded samples from the various angles were subjected to selected service related mechanical tests and microstructural...
متن کاملEffects of Heat Treatment on Strength and Ductility of Rolled and Forged Aluminum 6063 Alloy
This work examines the effect of heat treatment on tensile strength and ductile responses of rolled and forged AA6063 aluminum alloy. Some cast samples were rolled while some were forged at ambient temperature (32C). The deformed samples were subjected to heat treatment processes. The tensile strengths of rolled (212 MPa) and forged (127 MPa) samples are enhanced at ambient temperature but with...
متن کاملStudy on Machining Parameters of TiB2 Reinforced Aluminum 6063 Composites
In this experimental study, three TiB2/Al metal matrix composites (MMCs) with 40 μm in mean size were produced using a melt stirring squeeze casting route. Test was carried out to find the parameters influencing surface roughness (Ra) and material removal rate (MRR) on machining the TiB2 reinforced Al-6063 composite materials. The orthogonal array, the signal-to-noise ratio, and analysis of var...
متن کاملSurface Roughening Behavior of 6063 Aluminum Alloy during Bulging by Spun Tubes
Severe surface roughening during the hydroforming of aluminum alloy parts can produce surface defects that severely restrict their application in the automobile and aerospace industry. To understand the relation between strain, grain size and surface roughness under biaxial stress conditions, hydro-bulging tests of aluminum alloy tubes were carried out, and the tubes with different grain sizes ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: DEStech Transactions on Materials Science and Engineering
سال: 2017
ISSN: 2572-889X
DOI: 10.12783/dtmse/icmsea/mce2017/10790