Preparation of Polyaniline/polyvinylalcohol nanocomposite and study its characterization after exposure to Laser Irradiation.
نویسندگان
چکیده
منابع مشابه
Preparation and Characterization of ZrO2/TiO2 Nanocomposite under Ultrasonic Irradiation by Sol-gel Route
TiO2/ZrO2 nanocomposite was obtained by the sonochemical technique. In this method, two separate gels containing zirconium and titanium were prepared and mixed together. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4. The precursor titanium tetra isopropoxide (TTIP) dissolved in isopropanol. Mixing of Titanium and Zirconium gels was resulted in a yellow TiO2/ZrO2 ...
متن کاملPreparation and Characterization of ZrO2/TiO2 Nanocomposite under Ultrasonic Irradiation by Sol-gel Route
TiO2/ZrO2 nanocomposite was obtained by the sonochemical technique. In this method, two separate gels containing zirconium and titanium were prepared and mixed together. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4. The precursor titanium tetra isopropoxide (TTIP) dissolved in isopropanol. Mixing of Titanium and Zirconium gels was resulted in a yellow TiO2/ZrO2 ...
متن کاملPreparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route
Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...
متن کاملPreparation and Characterization of ZrO2/ZnO Nanocomposite under Ultrasonic Irradiation via Sol-gel Route
Nanocomposite of ZrO2/ZnO was prepared under ultrasonic irradiation by sol gel process from directly mixing Zirconium and Zinc gels, and the mixture was placed under ultrasonic irradiation for 2 hours then aging time the filtrated composite gel was calcinated at 500°C for 3h in furnace. The precursor sol of zirconium was prepared from an aqueous solution of ZrCl4 and zinc acetate dihydrated was...
متن کاملthe study of practical and theoretical foundation of credit risk and its coverage
پس از بررسی هر کدام از فاکتورهای نوع صنعت, نوع ضمانت نامه, نرخ بهره , نرخ تورم, ریسک اعتباری کشورها, کارمزد, ریکاوری, gdp, پوشش و وثیقه بر ریسک اعتباری صندوق ضمانت صادرات ایران مشخص گردید که همه فاکتورها به استثنای ریسک اعتباری کشورها و کارمزد بقیه فاکتورها رابطه معناداری با ریسک اعتباری دارند در ضمن نرخ بهره , نرخ تورم, ریکاوری, و نوع صنعت و ریسک کشورها اثر عکس روی ریسک اعتباری داردو پوشش, وثی...
15 صفحه اولذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Scientific Research in Science
سال: 2015
ISSN: 2356-8372
DOI: 10.21608/jsrs.2015.19951