Preparation of Ni–Zn–Cu ferrite particles by sol–gel technique
نویسندگان
چکیده
منابع مشابه
New Technique to Make Ferrite Nanosized Particles
Preparation of magnetitelmaghemite nanometric particles is reported from the precipitation of ferrous dodecyl sulfate micellar solution with methylamine. The size of nanocrystals is controlled by the micellar concentration and by temperature. It varies from 3.3nm to llnm. Magnetic properties are studied for various sizes of maghemite particles.
متن کاملPreparation and magnetic properties of nano size nickel ferrite particles using hydrothermal method
BACKGROUND Nickel ferrite, a kind of soft magnetic materials is one of the most attracting class of materials due to its interesting and important properties and has many technical applications, such as in catalysis, sensors and so on. In this paper the synthesis of NiFe2O4 nanoparticles by the hydrothermal method is reported and the inhibition of surfactant (Glycerol or Sodium dodecyl sulfate)...
متن کاملPreparation of high-permeability NiCuZn ferrite.
Appropriate addition of CuO/V2O5 and the reduction of the granularity of the raw materials particle decrease the sintering temperature of NiZn ferrite from 1200 degrees C to 930 degrees C. Furthermore, the magnetic properties of the NiZn ferrite prepared at low temperature of 930 degrees C is superior to that of the NiZn ferrite prepared by sintering at high temperature of 1200 degrees C becaus...
متن کاملPreparation and investigation of magnetic properties of Manganese Cadmium ferrite nanoparticles by Sol-gel method
In the present investigation, manganese ferrite nanoparticles substituted by cadmium with Mn1-xCdxFe2O4 composition and substituted amount x=(0, 0.1, 0.3, 0.5) were prepared by Sol-gel method. Pattern analysis of X-ray diffraction (XRD) confirmed ferrite single phase structure in all samples. The average crystal size was estimated from 17 to 22 nm. The chemical bonds and ferrite formation phase...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Materials Letters
سال: 2006
ISSN: 0167-577X
DOI: 10.1016/j.matlet.2006.01.093