Preparation of NiZn Ferrite Films by Ultrasound-Enhanced Ferrite Plating

New Developments in Ferrite Plating

The ferrite plating a method synthesizing ferrite films from an aqueous solution -has developed lately as follows; (1) Applying power ultrasound to aqueous solution improves the qualities of ferrite coating on polymer microspheres much, (2) similarity is found between mechanisms of the ferrite plating and bacterial FesO4 ( magnetsome) synthesis, (3) using highly alkaline (pH=13) solution contai...

Induction of apoptosis in cancer cells by NiZn ferrite nanoparticles through mitochondrial cytochrome C release

The long-term objective of the present study was to determine the ability of NiZn ferrite nanoparticles to kill cancer cells. NiZn ferrite nanoparticle suspensions were found to have an average hydrodynamic diameter, polydispersity index, and zeta potential of 254.2 ± 29.8 nm, 0.524 ± 0.013, and -60 ± 14 mV, respectively. We showed that NiZn ferrite nanoparticles had selective toxicity towards ...

Preparation of high-permeability NiCuZn ferrite.

Appropriate addition of CuO/V2O5 and the reduction of the granularity of the raw materials particle decrease the sintering temperature of NiZn ferrite from 1200 degrees C to 930 degrees C. Furthermore, the magnetic properties of the NiZn ferrite prepared at low temperature of 930 degrees C is superior to that of the NiZn ferrite prepared by sintering at high temperature of 1200 degrees C becaus...

Textured Growth of Strontium Ferrite Thin Films by Sputtering

M-Type Barium Hexagonal Ferrite Films