Preparation of nanocrystalline cellulose via ultrasound and its reinforcement capability for poly(vinyl alcohol) composites
نویسندگان
چکیده
منابع مشابه
Nanofiber composites of polyvinyl alcohol and cellulose nanocrystals: manufacture and characterization.
Cellulose nanocrystals (CN) were used to reinforce nanofibers in composite mats produced via electrospinning of poly(vinyl alcohol) (PVA) with two different concentrations of acetyl groups. Ultrathin cross-sections of the obtained nanocomposites consisted of fibers with maximum diameters of about 290 nm for all the CN loads investigated (from 0 to 15% CN loading). The electrospinning process di...
متن کاملShort Cellulose Nanofibril/polyvinyl Alcohol Nanocomposite Fibers
Short cellulose nanofibrils (SCNF) were investigated as a reinforcement for polyvinyl alcohol (PVA) fibers. SCNF fibers were mechanically isolated from hard wood pulp after enzymatic pretreatment. Various levels of SCNF were added to PVA and gel-spun into continuous fibers. The molecular orientation of PVA was affected by a combination of wet drawing during gel spinning and post-hot-drawing at ...
متن کاملPreparation and Characterization of Polyvinyl Alcohol-Chitosan Composite Films Reinforced with Cellulose Nanofiber
In this study microcrystalline cellulose (MCC) was oxidized by 2,2,6,6-tetramethylpiperidine-1-oxyl radical (TEMPO)-mediated oxidation. The treated cellulose slurry was mechanically homogenized to form a transparent dispersion which consisted of individual cellulose nanofibers with uniform widths of 3-4 nm. Bio-nanocomposite films were then prepared from a polyvinyl alcohol (PVA)-chitosan (CS) ...
متن کاملBiodegradable single-polymer composites from polyvinyl alcohol
The microstructure and thermomechanical behaviour of a novel fully biodegradable polyvinyl alcohol (PVOH)-based single-polymer composite (SPC) is presented. Three kinds of PVOH stapled fibres, having different melting temperatures and tensile mechanical properties, were considered as a reinforcement, whilst plasticized PVOH granules were selected as a continuous matrix. Calorimetric tests on th...
متن کاملPreparation and Characterization of Waterborne Polyurethane Modified by Nanocrystalline Cellulose
Nanocrystalline cellulose (NCC) was used as a modifier for waterborne polyurethane (WPU) to investigate the water and ethanol resistance of WPU-NCC composites. The NCC surface was modified with γ-glycidoxypropyltrimethoxysilane (GPTMS) and γammnonimpropylmethyldimethoxysilane (APMDS) to improve its compatibility with waterborne polyurethane (WPU), as indicated by the contact angle (CA). The cha...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Ultrasonics Sonochemistry
سال: 2012
ISSN: 1350-4177
DOI: 10.1016/j.ultsonch.2011.11.007