Preparation of MgAl2O4 Spinel Powder by Corrosion Reaction Synthesis
نویسندگان
چکیده
منابع مشابه
Preparation of nanostructured nickel aluminate spinel powder from spent NiO/Al2O3 catalyst by mechano-chemical synthesis
0921-8831/$ see front matter 2011 The Society of doi:10.1016/j.apt.2011.11.004 ⇑ Corresponding author. Address: School of Metallu ing, University of Tehran, P.O. Box 14395-1491, Tehran fax: +98 21 88006076. E-mail address: [email protected] (S. Sheibani). In this paper, the possibility of mechano-chemical synthesis, as a single step process for preparation of nanostructured nickel aluminate sp...
متن کاملLOW TEMPERATURE SYNTHESIS OF NANOCRYSTALLINE MgAl2O4 SPINEL VIA SUCROSE PROCESS
Abstract: Nanocrystalline MgAl2O4 spinel powder was synthesized using metal nitrates and a polymer matrix-based composed of sucrose and polyvinyl alcohol (PVA). The precursor and the calcined powders were characterized by simultaneous thermal analysis (STA), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), and scanning electron microscopy (SEM). According to XRD res...
متن کاملSynthesis & Characterization of CaB4O7 Powder by Solid-State Reaction
The synthesis of calcium tetraborate was investigated in a temperature ranging from 800℃ to 900℃ using the solid-state reaction method. The synthesis was done using ammonium tetraborate tetrahydrate as the source of boron. At temperatures of 800 ℃ and 880 ℃, the mixed phases from different compounds were formed. At the optimum temperature of 840℃, the mixed phase was only composed of meta and t...
متن کاملLOW TEMPERATURE MOLTEN SALT SYNTHESIS OF NANO CRYSTALLINE MgAl2O4 POWDER
Abstract: composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nanopowder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-Teller (BET) techniques. It was demonstrated tha...
متن کاملSYNTHESIS OF MgAl2O4-Ti(C,N) NANOCOMPOSITE BY ALUMINOTHERMIC REDUCTION
MgAl2O4/Ti(C,N) composites were synthesized through aluminothermic reaction between Al,TiO 2,MgO powders and phenolic resin in coke bed condition. Effect of addition of carbon black and sugar into the mixture at different temperatures were investigated. The phases and microstructures of samples were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). MgAl 2O4 ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of the Japan Society of Powder and Powder Metallurgy
سال: 2012
ISSN: 0532-8799,1880-9014
DOI: 10.2497/jjspm.59.29