Preparation of lanthanum ferrite powder at low temperature
نویسندگان
چکیده
منابع مشابه
Preparation of Fe3Si/Ferrite Micro- and Nano-Powder Composite
Composite material based on Fe3Si micro-particles and Mn-Zn nano-ferrite was prepared using powder metallurgy technology. The sol-gel followed by autocombustion process was used for synthesis of Mn0.8Zn0.2Fe2O4 ferrite. 3 wt.% of mechanically milled ferrite was mixed with Fe3Si powder alloy. Mixed micro-nano powder system was homogenized by the Resonant Acoustic Mixing using ResodynLabRAM Mixer...
متن کاملSynthesize of Superparamagnetic Zinc Ferrite Nanoparticles at Room Temperature
Superparamagnetic single phase zinc ferrite nanoparticles have been prepared by coprecipitation method at 20 °C without any subsequent calcination. The composition, crystallite size, microstructure and magnetic properties of the prepared nanoparticles were investigated using X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), transmission electron microscope (TEM)...
متن کاملTemperature dependence of magnetic anisotropy constant in manganese ferrite nanoparticles at low temperature
The temperature dependence of the effective magnetic anisotropy constant, K(T), of MnFe2O4 nanoparticles is obtained based on superconducting quantum interference device magnetometry measurements. The variation of the blocking temperature, TB, as a function of particle radius, r, is first determined by associating the particle size distribution and the anisotropy energy barrier distribution ded...
متن کاملLOW TEMPERATURE MOLTEN SALT SYNTHESIS OF NANO CRYSTALLINE MgAl2O4 POWDER
Abstract: composition of MgO and nano boehmite. The reactant and potassium chloride, as the reaction media, were fired at800-1000 °C at different dwell times (0.5-5 h) in the ambient atmosphere. After washing and filtration, the spinel nanopowder was characterized by X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Brunauer-Emmett-Teller (BET) techniques. It was demonstrated tha...
متن کاملSynthesis and characterization of Lanthanum doped Bismuth Ferrite
B1-xLaxFeO3 (x = 0.0, 0.025) crystallites were prepared by chemical solution route. XRD analysis confirmed the phase formation of the materials. Thermal characterization was done by DSC-TGA to confirm crystallization and thermal behavior for phase development. Morphological studies by FESEM showed the agglomerated nature of the ferrite...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Cerâmica
سال: 2012
ISSN: 0366-6913
DOI: 10.1590/s0366-69132012000100020