Preparation of activated carbon with high surface area for high-capacity methane storage
نویسندگان
چکیده
منابع مشابه
Preparation of High Surface Area ZrO2 Nanoparticles
In comparison to the previous researches, ZrO2 nanoparticles with higher surface area (85 m2/g) have been synthesized in this research. The as-prepared ZrO2 nanoparticles by co-precipitation method were characterized with X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The surface area of the s...
متن کاملPreparation and Characterization of High Surface Area Activated Carbon Fibers from Lignin
Activated carbon fibers (ACFs) were successfully prepared from softwood lignin, which was isolated with polyethylene glycol 400 (PEG-400) as a solvolysis reagent, by water steam activation. The pore characterization and adsorption property of ACFs were investigated. The results showed that all the ACFs with more micropores exhibited high specific surface area and total pore volume which increas...
متن کاملA Procedure for Preparation of Semi-activated Carbon Fiber without any Treatment under High Temperature
A procedure for preparation of semi-activated carbon fiber (SACF) without any treatment under high temperature was proposed. The first step of the procedure is coating of an inorganic fiber (E-glass fiber) by an adsorbent mixture including powder activated carbon, methyl cellulose and water. In this work a set of experiments was performed to attain appropriate adsorbent mixture for good quality...
متن کاملpreparation of high surface area zro2 nanoparticles
in comparison to the previous researches, zro2 nanoparticles with higher surface area (85 m2/g) have been synthesized in this research. the as-prepared zro2 nanoparticles by co-precipitation method were characterized with x-ray diffraction (xrd), scanning electron microscopy (sem) and transmission electron microscopy (tem). the surface area of the sample was characterized by bet method. the eff...
متن کاملPreparation, Surface and Pore Structure of High Surface Area Activated Carbon Fibers from Bamboo by Steam Activation
High surface area activated carbon fibers (ACF) have been prepared from bamboo by steam activation after liquefaction and curing. The influences of activation temperature on the microstructure, surface area and porosity were investigated. The results showed that ACF from bamboo at 850 °C have the maximum iodine and methylene blue adsorption values. Aside from the graphitic carbon, phenolic and ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Journal of Energy Chemistry
سال: 2014
ISSN: 2095-4956
DOI: 10.1016/s2095-4956(14)60198-4