Activated Carbon Monolith Derived from Polymer and Fast Pyrolytic Char: Effect of Bio-Oil Phenol- Formaldehyde Resin
Activated carbon monoliths (ACMs) were fabricated by H2O activation using powdered fast pyrolytic char (PFPC) as a raw material and bio-oil phenol-formaldehyde (BPF) resin as a binder. The effects of the ratio of BPF resin to PFPC on textural and chemical-surface properties of the ACMs were investigated using elemental analysis, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (...
متن کاملFabrication of Glass Fiber Reinforced Composites Based on Bio-Oil Phenol Formaldehyde Resin
In this study, bio-oil from fast pyrolysis of renewable biomass was added by the mass of phenol to synthesize bio-oil phenol formaldehyde (BPF) resins, which were used to fabricate glass fiber (GF) reinforced BPF resin (GF/BPF) composites. The properties of the BPF resin and the GF/BPF composites prepared were tested. The functional groups and thermal property of BPF resin were thoroughly inves...
متن کاملPreparation and Characterization of a Phenol-formaldehyde Resin Adhesive Obtained From Bio-ethanol Production Residue
Phenol formaldehyde (PF) resins are widely used as wood adhesives in the industrial production of exterior-grade plywood panels, oriented strand board panels and particleboards due to their superior performance including high bonding strength, heat resistance, excellent water resistance and chemical stability1. However, phenol, one raw material for the synthesis of PF resins, is a petroleum-bas...
متن کاملSynthesis and Characterization of Bio-Oil Phenol Formaldehyde Resin Used to Fabricate Phenolic Based Materials
In this study, bio-oil from the fast pyrolysis of renewable biomass was used as the raw material to synthesize bio-oil phenol formaldehyde (BPF) resin-a desirable resin for fabricating phenolic-based material. During the synthesis process, paraformaldehyde was used to achieve the requirement of high solid content and low viscosity. The properties of BPF resins were tested. Results indicated tha...
متن کاملPreparation and characterization of carbon materials from phenol formaldehyde resin with pore forming substance
This paper describes the carbonization behavior of phenol-formaldehyde resin (PF) blended in the presence of simple organic substances of m-phthalic acid (PA), trimesic acid (TMA) and phloroglucinol (PG). The weight loss and heat flow were monitored in order to study their carbonization behavior by thermogravimetric analysis (TG) and differential scanning calorimetry (DSC), respectively. These ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: BioResources
سال: 2015
ISSN: 1930-2126
DOI: 10.15376/biores.10.3.3865-3873