Preparation and Properties of Wood Plastic Composites with Desirable Features Using Poplar and Five Recyclable Plastic Wastes
نویسندگان
چکیده
This study evaluated the mechanical and hydrophobic properties of wood plastic composites (WPC) prepared by hot molding approach incorporating five different recycled plastics poplar flour. The WPC showed excellent tensile strength (36.9 MPa) flexural (44.7 associated with good hydrophobicity, could be due to application pressing which improved amount hydroxyl groups reduced crystallinity WPC. also revealed a strong hydrostable structure negligible emission formaldehyde during preparation process. Overall, used substitute traditional wood-based panels as potential furniture material, hence achieving sustainable utilization wastes.
منابع مشابه
Durability of wood plastic composites manufactured from recycled plastic
The influence of accelerated weathering, xenon-arc light and freeze-thaw cycling on wood plastic composites extruded from a recycled plastic was studied. The results showed that, in general, weathering had a stronger impact on samples made from plastic waste compared to a sample made from virgin material. After weathering, the mechanical properties, tensile and flexural, were reduced by 2-30%, ...
متن کاملSome of the Properties of Wood Plastic Composites
In this study some of the important properties of experimentally manufactured wood– plastic composites (WPC) were determined. Specimen having 60% and 80% particle and fibre of radiata pine (Pinus radiata ) were mixed with polypropylene (plastic) and four different additives, namely Struktol TR 016 which is coupling agent, CIBA antimicrobial agent (IRGAGUARD F3510) as fungicide, CIBA UV filter c...
متن کاملProperties of Flat-Pressed Wood Plastic Composites Containing Fire Retardants
This study investigated physical, mechanical, and fire properties of the flat-pressed wood plastic composites (WPCs) incorporated with various fire retardants (FRs) [5 or 15% by weight (wt)] at 50 wt % of the wood flour (WF). The WPC panels were made from dryblended WF, polypropylene (PP) with maleic anhydridegrafted PP (2 wt %), and FR powder formulations using a conventional flat-pressing pro...
متن کاملthermal properties of wood-plastic composites prepared from hemicellulose-extracted wood flour
hemicellulose of southern yellow pine wood spices was extracted by pressurized hot water at three different temperatures: 140°c, 155°c and 170°c. compounding with pp (polypropylene) was performed by extrusion after preparing wood flour and sieving to determine its mesh size. the ratio of wood to polymer was 50:50 based on oven-dry weight of wood flour. all extraction treatments and control samp...
متن کاملFiber reinforced plastic composites using recycled materials
This work investigates the feasibility of using recycled high density polyethylene (rHDPE), recycled polypropylene (rPP) and old newsprint fiber (ONP) to manufacture fiber reinforced composites. The boards were made through air-forming and hot press. The effects of the fiber loading and coupling agent content on tensile, flexural, internal bond properties and water absorption and thickness swel...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: Applied sciences
سال: 2021
ISSN: ['2076-3417']
DOI: https://doi.org/10.3390/app11156838