Preparation and Properties of MgO-TiO2-CeO2-ZrO2 Composite Materials
نویسندگان
چکیده
منابع مشابه
Porous Composite Materials ZrO2(MgO)-MgO for Osteoimplantology
The pore structure and phase composition of ceramic composite material ZrO2(Mg)-MgO at different sintering temperatures were studied. The main mechanical characteristics of the material were determined and it was shown that they are close to the characteristics of natural bone tissues. It was shown that material structure has a positive effect on the pre-osteoblast cells proliferation. In-vitro...
متن کاملAnatase TiO2 and mixed M-Anatase TiO2 (M = CeO2 or ZrO2) nano powder: Synthesis and characterization
Pure Anatase Titania (TiO2), mixed 1.0 wt.% Cerium-Anatase Titania (1.0 wt.%CeO2-TiO2), and mixed 1.0 wt.% Zirconia-Anatase Titania (1.0 wt.%ZrO2-TiO2) nano powders were synthesized by co-precipitation method and characterized using X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) surface area analysis, UV-Vis diffuse reflectance spect...
متن کاملComparison of mechanical properties of the Zro2 and TiO2 filler epoxy composite
---------------------------------------------------------------------***--------------------------------------------------------------------Abstract Effect of TiO2 and ZrO2 filler on mechanical properties of the epoxy polymer has been investigated experimentally. TiO2 and ZrO2 filler epoxy composites are fabricated by hand layup technique in a mold and cured under light pressure at room tempera...
متن کاملAnatase TiO2 and mixed M-Anatase TiO2 (M = CeO2 or ZrO2) nano powder: Synthesis and characterization
Pure Anatase Titania (TiO2), mixed 1.0 wt.% Cerium-Anatase Titania (1.0 wt.%CeO2-TiO2), and mixed 1.0 wt.% Zirconia-Anatase Titania (1.0 wt.%ZrO2-TiO2) nano powders were synthesized by co-precipitation method and characterized using X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) surface area analysis, UV-Vis diffuse reflectance spect...
متن کاملStructure and electrical properties of sputtered TiO2/ZrO2 bilayer composite dielectrics upon annealing in nitrogen
The high-k dielectric TiO2/ZrO2 bilayer composite film was prepared on a Si substrate by radio frequency magnetron sputtering and post annealing in N2 at various temperatures in the range of 573 K to 973 K. Transmission electron microscopy observation revealed that the bilayer film fully mixed together and had good interfacial property at 773 K. Metal-oxide-semiconductor capacitors with high-k ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
ژورنال
عنوان ژورنال: IOP Conference Series: Materials Science and Engineering
سال: 2019
ISSN: 1757-899X
DOI: 10.1088/1757-899x/493/1/012094