Preparation and luminescence of bulk oxyfluoride glasses doped with Ag nanoclusters

Preparation and luminescence of bulk oxyfluoride glasses doped with Ag nanoclusters.

Bulk oxyfluoride glasses doped with Ag nanoclusters have been prepared using the melt quenching technique. When pumped in the absorption band of Ag nanoclusters between 300 to 500 nm, these glasses emit a very broad luminescence band covering all the visible range with a weak tail extending into the near infrared. The maximum of the luminescence band and its color shifts to the blue with a shor...

Luminescence Properties of Oxyfluoride Glass and Glass Ceramic Doped with Y3 + Ions

 Oxyfluoride glass ceramics containing CaF2nano-crystals doped with Y3+ ions were prepared by one-step crystallization of SiO2- Al2O3- CaO- CaF2 glasses at different temperatures. X- ray diffraction (XRD) results have revealed that CaF2 was the only precipitated crystalline phase in glass ceramic samples. According to the XRD results, a glass ceramic was selected as the best sample in order to ...

Development of ytterbium-doped oxyfluoride glasses for laser cooling applications

Oxyfluoride glasses doped with 2, 5, 8, 12, 16 and 20 mol% of ytterbium (Yb(3+)) ions have been prepared by the conventional melt-quenching technique. Their optical, thermal and thermo-mechanical properties were characterized. Luminescence intensity at 1020 nm under laser excitation at 920 nm decreases with increasing Yb(3+) concentration, suggesting a decrease in the photoluminescence quantum ...

Upconversion luminescence in Er-doped germanate-oxyfluoride and tellurium-germanate-oxyfluoride transparent glass-ceramics

Upconversion luminescence has been studied for Er in a germanate-oxyfluoride and a tellurium-germanate-oxyfluoride transparent glass-ceramic using 800 nm excitation. Significantly increased upconversion luminescence was observed from transparent glass-ceramics compared with that from their corresponding as-prepared glasses. In addition to a strong green emission centered at 545 nm from S3/2 sta...

Synthesis and luminescence of uniform europium- doped bismuth fluoride and bismuth oxyfluoride particles with different morphologies†